materiali senza amianto per guarnizioni non-asbestos

NON-ASBESTOS COMPRESSED
FIBRE JOINTINGS AND
EXPANDED GRAPHITE JOINTINGS
MATERIALI SENZA AMIANTO
PER GUARNIZIONI
FMI catalogo AMIANTO 06m08.indd 1
18-06-2008 11:08:57
FMI catalogo AMIANTO 06m08.indd 2
18-06-2008 11:08:58
FMI catalogo AMIANTO 06m08.indd 3
18-06-2008 11:09:16
AF 163
DESCRIZIONE
Fogli a base di Fibre sintetiche, minerali, aramidiche con legante in gomma NBR.
Colore verde chiaro.
IMPIEGHI
È raccomandata per impieghi non gravosi con
medie temperature e medie pressioni e molti
agenti chimici.
TEMP. MAX RACCOMANDATA:
210°C (410°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.81
compressibilità ASTM
%
10
ritorno elastico ASTM
%
54
resistenza a trazione ASTM
MPa
8
permeabilità ai gas DIN
ml/min 0.1
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
17
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
10
MISURE DISPONIBILI
lastre
mm 1500x1500
mm 1500x3000
mm 2000x2000
spessori
da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
7 Mpa (70 bar)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
16
16
3
3
AF
AF
16
1
3
63
AF
AF
A
3
16
1
AF
DESCRIPTION
AF 163 is a natural/nitrile rubber based asbestos-free sheet sealing material reinforced with
cellulose and aramid fibres, with surfaces specially formulated to further enhance the sealing
characteristics.
Colour green.
SERVICE
AF 163 is recommended for low temperature,
medium pressure applications. It is particularly
suitable for sealing hot and cold water and mild
chemicals.
MAXIMUM RECOMMENDED TEMP.:
210°C (410°F)
MAXIMUM RECOMMENDED PRESSURE:
7 Mpa (70 bar)
3
1
AF
63
1
AF
6
F1
3
16
63
AF
63
AF
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
16
3
16
3
mm
1.50
g/cmc 1.81
%
10
%
54
MPa
8
ml/min 0.1
%
17
%
10
AVAILABILITY
sheet size
mm 1500x1500
mm 1500x3000
mm 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
4
FMI catalogo AMIANTO 06m08.indd 4
18-06-2008 11:09:17
AF 192
DESCRIZIONE
Fogli a base di Fibre aramidiche (Kevlar®) con legante in gomma NR/NBR a rigonfiamento controllato.
Colore verde scuro.
IMPIEGHI
È raccomandata per utilizzi in presenza di olii,
carburanti, refrigeranti, gas e molti agenti chimici. Adatta per usi cantieristici, navali e per impieghi motoristici. Per l’elevato valore di ritorno elastico e comprimibilità è particolarmente adatta
in impieghi di manutenzione su flange usurate
o disassate.
TEMP. MAX RACCOMANDATA:
350°C (660°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.80
compressibilità ASTM
%
19
ritorno elastico ASTM
%
58
resistenza a trazione ASTM
MPa
10
permeabilità ai gas DIN
ml/min≤0.1
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
≤8.5
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
9
ASTM OIL 3 assorbimento
5 ore a 20°C
%
15
ASTM FUEL B assorbimento
5 ore a 20°C
%
14
MISURE DISPONIBILI
lastre
mm 1500x1500, 1500x3000, 2000x2000
spessori da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
10 Mpa (100 bar)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
19
19
2
2
AF
AF
19
1
2
92
AF
AF
A
2
19
1
AF
DESCRIPTION
AF 192 is nitrile rubber based, asbestos-free
sheet sealing material reinforced with aramid
and glass fibres.
Colour dark green.
SERVICE
AF 192 is suitable for use in applications involving hot and cold water, oils, fuels, and a wide
range of non-aggressive chemicals. AF 192 can
be used in shipyard and mechanical industries.
Recommended for worn flanges.
MAXIMUM RECOMMENDED TEMP.:
350°C (660°F)
MAXIMUM RECOMMENDED PRESSURE:
10 Mpa (100 bar)
2
1
AF
92
1
AF
9
F1
2
19
92
AF
92
AF
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
ASTM OIL 3 weight increase
5 h at 20°C
ASTM FUEL B weight increase
5 h at 20°C
19
2
19
2
mm
1.50
g/cmc 1.80
%
19
%
58
MPa
10
ml/min ≤0.1
%
≤8.5
%
9
%
15
%
14
AVAILABILITY
sheet size mm 1500x1500, 1500x3000, 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
5
FMI catalogo AMIANTO 06m08.indd 5
18-06-2008 11:09:50
AF 240
DESCRIZIONE
Fogli a base di Fibre aramidiche con legante in
gomma NBR di elevata qualità.
Colore blu.
IMPIEGHI
È adatta per usi universali nell’industria chimica,
a contatto con olii, carburanti e svariati agenti
chimici.
TEMP. MAX RACCOMANDATA:
350°C (660°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.84
compressibilità ASTM
%
7.7
ritorno elastico ASTM
%
≥50
resistenza a trazione ASTM
MPa ≥13
permeabilità ai gas DIN
ml/min≤0.3
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
≤10
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
11
MISURE DISPONIBILI
lastre
mm 1500x1500
mm 1500x3000
mm 2000x2000
spessori
da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
10 Mpa (100 bar)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
24
24
0
0
AF
AF
24
2
0
40
AF
AF
0
2
AF
40
2
AF
4
F2
0
24
A
0
24
2
AF
40
AF
40
AF
SERVICE
AF 240 is suitable for use in applications involving hot and cold water, steam, oils, fuels, gases,
and a wide range of general chemicals.
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
MAXIMUM RECOMMENDED TEMP.:
350°C (660°F)
AVAILABILITY
sheet size
DESCRIPTION
AF 240 is nitrile rubber based, asbestos-free
sheet sealing material reinforced with synthetic
fibres.
Colour blue.
MAXIMUM RECOMMENDED PRESSURE:
10 Mpa (100 bar)
24
0
24
0
mm
g/cmc
%
%
MPa
ml/min
1.50
1.84
7.7
≥50
≥13
≤0.3
%
≤10
%
11
mm 1500x1500
mm 1500x3000
mm 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
6
FMI catalogo AMIANTO 06m08.indd 6
18-06-2008 11:10:08
AF 280
TEMP. MAX RACCOMANDATA:
400°C (750°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.84
compressibilità ASTM
%
7.5
ritorno elastico ASTM
%
56
resistenza a trazione ASTM
MPa
16
permeabilità ai gas DIN
ml/min 0.2
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
2
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
3.4
ASTM OIL 3 assorbimento
5 ore a 150°C
%
7.4
ASTM FUEL B assorbimento
5 ore a 150°C
%
10.2
PRESS. MAX RACCOMANDATA:
12 Mpa (120 bar)
MISURE DISPONIBILI
lastre
mm 1500x1500, 1500x3000, 2000x2000
spessori da mm 0.5 a mm 5.0
DESCRIZIONE
Fogli a base di Fibre aramidiche (Kevlar®) e legante in gomma NBR ad alto tenore acrilonitrilico.
Colore nero.
IMPIEGHI
È adatta per svariate applicazioni industriali, fra
cui vapore saturo, solventi e molti agenti chimici,
inclusi alcali forti.
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
28
28
0
0
AF
AF
28
2
0
80
AF
AF
A
0
28
2
AF
DESCRIPTION
AF 280 is an aramid fibre based sheet sealing
material bound with a high quality nitrile rubber.
Colour black.
SERVICE
AF 280 is suitable for use across a broad spectrum of industrial applications involving steam
(including super-heated steam), water, oils, solvents, fuels, gases, general chemicals, diluite acids and alkalis.
MAXIMUM RECOMMENDED TEMP.:
400°C (750°F)
MAXIMUM RECOMMENDED PRESSURE:
12 Mpa (120 bar)
0
2
AF
80
2
AF
8
F2
0
28
80
AF
80
AF
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
ASTM OIL 3 weight increase
5 h at 150°C
ASTM FUEL B weight increase
5 h at 150°C
mm
g/cmc
%
%
MPa
ml/min
28
0
28
0
1.50
1.84
7.5
56
16
0.2
%
2
%
3.4
%
7.4
%
10.2
AVAILABILITY
sheet size mm 1500x1500, 1500x3000, 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
7
FMI catalogo AMIANTO 06m08.indd 7
18-06-2008 11:10:27
AFK 250
DESCRIZIONE
Fogli a base di Fibre aramidiche (Kevlar®) protette da fibre inorganiche e legante in gomma
Hypalon.
Colore bianco.
IMPIEGHI
È studiata appositamente per usi gravosi in ambito chimico, a contatto con acidi organici e
inorganici forti, alcali, solventi, fenoli, dimetilfenoli ed altri.
TEMP. MAX RACCOMANDATA:
200°C (390°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.80
compressibilità ASTM
%
9.4
ritorno elastico ASTM
%
49
resistenza a trazione ASTM
MPa
8
permeabilità ai gas DIN
ml/min 0.54
incremento di volume in:
ACIDO SOLFORICO al 98%
18 ore a 20°C
%
<10
ACIDO NITRICO al 50%
1 ora a 65°C
%
<8
MISURE DISPONIBILI
lastre
mm 1500x1500
mm 1500x3000
mm 2000x2000
spessori
da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
6 Mpa (60 bar; 870 psi)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
K2
K
AF
50
25
0
AF
AF
K2
K2
50
50
AF
AF
K
0
25
K2
50
DESCRIPTION
AFK 250 is an acid resistant calendered sheet sealing material reinforced with a lend of organic and
inorganic fibres and bound in a specially formulated synthetic rubber binder matrix.
Colour white.
SERVICE
AFK 250 is specially recommended for use in applications where mineral acids have to be sealed.
It gives excellent performance in concentrated sulphuric and hydrochloric acids and can be used to
seal nitric at concentrations up to 50% and temperatures up to 65°C. AFK 250 can be also be used
to seal a wide range of chemicals including oils,
fuels, solvents, alkalis, water and steam.
MAXIMUM RECOMMENDED TEMP.:
200°C (390°F)
MAXIMUM RECOMMENDED PRESSURE:
6 Mpa (60 bar; 870 psi)
AF
AF
5
K2
0
5
K2
0
A
2
FK
AF
50
5
K2
AF
0
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
thickness increase
98% SULPHURIC ACID
18 h at 20°C
50% NITRIC ACID
1 h at 65°C
K2
K
AF
50
25
0
mm
g/cmc
%
%
MPa
ml/min
1.50
1.80
9.4
49
8
0.54
%
<10
%
<8
AVAILABILITY
sheet size
mm 1500x1500
mm 1500x3000
mm 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
8
FMI catalogo AMIANTO 06m08.indd 8
18-06-2008 11:10:47
AFM 280
DESCRIZIONE
Fogli a base di Fibre aramidiche (Kevlar®) e legante in gomma NBR ad alto tenore acrilonitrilico e rinforzo in rete metallica.
TEMP. MAX RACCOMANDATA:
425°C (800°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 2.2
compressibilità ASTM
%
8.5
ritorno elastico ASTM
%
≥56
resistenza a trazione ASTM
MPa ≥23
permeabilità ai gas DIN
ml/min≤0.2
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
2
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
3.4
ASTM OIL 3 assorbimento
5 ore a 150°C
%
7
ASTM FUEL B assorbimento
5 ore a 150°C
%
10.2
PRESS. MAX RACCOMANDATA:
12 Mpa (120 bar)
MISURE DISPONIBILI
lastre
mm 1500x1500, 1500x3000, 2000x2000
spessori da mm 0.5 a mm 5.0
Colore nero.
IMPIEGHI
È adatta per gli stessi impieghi ove si utilizza la
AF 280, e nei casi in cui sia richiesta una elevata
coppia di serraggio dei bulloni.
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
M
M
AF
28
28
0
0
AF
AF
M
M
2
80
28
0
AF
AF
M
M
0
28
0
28
DESCRIPTION
AFM 280 is an aramid fibre based sheet sealing material bound with a high quality nitrile rubber. Sealing
performance and blow-out resistance are further enhanced by the inclusion of a steel wire gauze.
Colour black.
SERVICE
AFM 280 is suitable for use across a broad spectrum
of industrial applications involving steam (including
super-heated steam), water, oils, solvents, fuels,
gases, general chemicals, diluite acids and alkalis.
AFM 280 is particularly suited for sealing in applications where flange movement caused by vibration
or thermal expansion may be experienced.
MAXIMUM RECOMMENDED TEMP.:
425°C (800°F)
MAXIMUM RECOMMENDED PRESSURE:
12 Mpa (120 bar)
AF
AF
M
M
28
0
28
0
A
FM
AF
M
28
0
28
0
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
DIN gas permeability
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
ASTM OIL 3 weight increase
5 h at 150°C
ASTM FUEL B weight increase
5 h at 150°C
AF
M
M
AF
mm
g/cmc
%
%
MPa
ml/min
28
0
28
0
1.50
2.2
8.5
≥56
≥23
≤0.2
%
2
%
3.4
%
7
%
10.2
AVAILABILITY
sheet size mm 1500x1500, 1500x3000, 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
9
FMI catalogo AMIANTO 06m08.indd 9
18-06-2008 11:11:08
AF 330
DESCRIZIONE
Fogli a base di Fibre aramidiche (Kevlar®) ad elevatissime performances con legante NBR/CR di
altissima qualità.
Colore naturale (beige).
IMPIEGHI
È adatta a sostituire le tradizionali giunture in
amianto di elevata qualità. Adatta per vapore
saturo, olio diatermico, solventi, acidi e basi a
bassa e media concentrazione.
TEMP. MAX RACCOMANDATA:
440°C
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm
1.50
peso specifico
g/cmc 1.68
compressibilità ASTM
%
12
ritorno elastico ASTM
%
≥63
resistenza a trazione ASTM
MPa
≥20
permeabilità ai gas DIN
ml/min ≤0.07
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
2
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
4
ASTM OIL 3 assorbimento
5 ore a 150°C
%
11
ASTM FUEL B assorbimento
5 ore a 150°C
%
13
MISURE DISPONIBILI
lastre
mm 1500x1500, 1500x3000, 2000x2000
spessori da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
14 Mpa (140 bar)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
33
33
0
0
AF
AF
33
3
0
30
AF
AF
A
0
33
3
AF
DESCRIPTION
AF 330 is a superior performance aramid fibre
sheet sealing material bound with a high quality
nitrile rubber.
Colour light yellow (pigment-free).
SERVICE
Developed for general industrial applications
where an asbestos free sheet is desirable, AF
330 is designed to be used at the same thickness
as the CAF material it replaces.
MAXIMUM RECOMMENDED TEMP.:
440°C
MAXIMUM RECOMMENDED PRESSURE:
14 Mpa (140 bar)
0
3
AF
30
3
AF
3
F3
0
33
30
AF
30
AF
33
0
33
0
TYPICAL PHYSICAL PROPERTIES
thickness
mm
1.50
density
g/cmc 1.68
ASTM compressibility
%
12
ASTM recovery
%
≥63
ASTM tensile strength
MPa
≥20
DIN gas permeability
ml/min ≤0.07
ASTM OIL 3 thickness increase
5 h at 150°C
%
2
ASTM FUEL B thickness increase
5 h at 150°C
%
4
ASTM OIL 3 weight increase
5 h at 150°C
%
11
ASTM FUEL B weight increase
5 h at 150°C
%
13
AVAILABILITY
sheet size mm 1500x1500, 1500x3000, 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
10
FMI catalogo AMIANTO 06m08.indd 10
18-06-2008 11:11:33
AF 500
DESCRIZIONE
Fogli a base di Fibre di carbonio pure rinforzate
con gomma NBR ad altissimo tenore acrilonitrilico.
Colore nero.
IMPIEGHI
È adatta a usi gravosi in presenza di vapore saturo e surriscaldato, olii diatermici, acidi e liquidi
fortemente alcalini PH 14.
TEMP. MAX RACCOMANDATA:
440°C (750°F)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm 1.50
peso specifico
g/cmc 1.75
compressibilità ASTM
%
7.5
ritorno elastico ASTM
%
64
resistenza a trazione ASTM
MPa 18.1
ASTM OIL 3 rigonfiamento
5 ore a 150°C
%
2.5
ASTM FUEL B rigonfiamento
5 ore a 150°C
%
4
ASTM OIL 3 assorbimento
5 ore a 150°C
%
10
ASTM FUEL B assorbimento
5 ore a 150°C
%
12
MISURE DISPONIBILI
lastre
mm 1500x1500, 1500x3000, 2000x2000
spessori da mm 0.5 a mm 5.0
PRESS. MAX RACCOMANDATA:
14 Mpa (140 bar; 2030 psi)
CERTIFICAZIONE Quality system accredited ISO 9001:2000
AF
AF
50
50
0
0
AF
AF
50
5
0
00
AF
AF
A
0
50
5
AF
DESCRIPTION
AF 500 is an NBR based, asbestos-free sheet
sealing material, reinforced with carbon an aramid fibres.
Colour black.
SERVICE
Suitable for use in a wide range of industrial applications including oils, fuels, steam, water and
dilute acids. AF 500 is especially suitable for sealing strong caustic liquors.
MAXIMUM RECOMMENDED TEMP.:
440°C (750°F)
MAXIMUM RECOMMENDED PRESSURE:
14 Mpa (140 bar; 2030 psi)
0
5
AF
00
5
AF
0
F5
0
50
00
AF
00
AF
TYPICAL PHYSICAL PROPERTIES
thickness
density
ASTM compressibility
ASTM recovery
ASTM tensile strength
ASTM OIL 3 thickness increase
5 h at 150°C
ASTM FUEL B thickness increase
5 h at 150°C
ASTM OIL 3 weight increase
5 h at 150°C
ASTM FUEL B weight increase
5 h at 150°C
50
0
50
0
mm
1.50
g/cmc 1.75
%
7.5
%
64
MPa 18.1
%
2.5
%
4
%
10
%
12
AVAILABILITY
sheet size mm 1500x1500, 1500x3000, 2000x2000
thickness range mm 0.5 to 5.0
CERTIFICATION Quality system accredited ISO 9001:2000
11
FMI catalogo AMIANTO 06m08.indd 11
18-06-2008 11:11:57
FGS 3
DESCRIZIONE
FGS 3 è un sandwich in grafite rinforzata da una
lamina arpionata in acciaio inox.
IMPIEGHI
FLEXIGRAF FGS 3 grazie all’inclusione del robusto strato di laminato arpionato è indicata per
applicazioni che richiedano alti valori di serraggio e dove siano richieste alte resistenze all’estrusione. L’FGS 3 è indicata per una svariata gamma di applicazioni industriali, fra le quali: vapore
saturo e surriscaldato, agenti chimici aggressivi
(eccetto ossidanti). Raccomandato nel campo
petrolchimico e termoelettrico ove sia richiesta
elevata resistenza al creep.
TEMP. MAX RACCOMANDATA:
550°C (1022°F) in ambiente ossidante
700°C (1290°F) in ambiente riducente o inerte
PRESS. MAX RACCOMANDATA:
20 Mpa (200 bar; 2900 psi)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm
1.5
densità (ASTM F1315)
g/cmc 1.5
comprimibilità (ASTM)
%
35
tensione residua (BS)
MPa
38
ritorno elastico (ASTM F152)
%
≥17
resistenza a trazione (ASTM F152) MPa ≥20
contenuto di ioni di cloro (ASTM 1277) ppm <50
contenuto di ioni di fluoro
ppm <25
contenuto di zolfo
ppm <995
MISURE DISPONIBILI
lastre
mm 1500x1500
mm 1000x1000
mm 1500x1000
spessori mm 0.5-0.75-1.0-1.5-2.0-3.0
CERTIFICAZIONE Quality system accredited ISO 9001:2000
FG
FG
S3
S3
FG
FG
S3
S3
S3
FG
3
FG
F
3
GS
FG
F
3
GS
S
FG
DESCRIPTION
FGS 3 is a graphite laminate reinforced with a
tanged stainless steel core.
SERVICE
FLEXIGRAF FGS 3 is recommended for applications involving high sealing stresses and where
high blowout resistance is required. The inclusion of the steel reinforcing layers give rise to a
robust sheet. FGS 3 can be used to seal a wide
range of media, with exception of strong oxidising agents at extremes of temperature and pressure. Typical industries where FGS 3 is used include power generation and petrochemical.
MAXIMUM RECOMMENDED TEMP.:
Oxidising media 550°C (1022°F)
Inert or reducing media 700°C (1292°F)
MAXIMUM RECOMMENDED PRESSURE:
20 Mpa (200 bar; 2900 psi)
S3
FG
S3
FG
S3
S3
TYPICAL PHYSICAL PROPERTIES
thickness
mm
1.5
density (ASTM F1315)
g/cmc 1.5
compressibility (ASTM)
%
35
residual stress (BS)
MPa
38
recovery (ASTM F152)
%
≥17
tensile strength (ASTM F152)
MPa ≥20
leachable chlorine ion content (ASTM 1277) ppm <50
leachable fluorine ion content
ppm <25
sulphur ion content
ppm <995
AVAILABILITY
sheet size
mm 1500x1500
mm 1000x1000
mm 1500x1000
thickness range mm 0.5-0.75-1.0-1.5-2.0-3.0
CERTIFICATION Quality system accredited ISO 9001:2000
12
FMI catalogo AMIANTO 06m08.indd 12
18-06-2008 11:12:23
FGS 4
DESCRIZIONE
FGS 4 è un sandwich in grafite rinforzata da una
lamina liscia in acciaio inox.
IMPIEGHI
FLEXIGRAF FGS 4 grazie all’inclusione del robusto strato di laminato è indicata per applicazioni
che richiedano alti valori di serraggio e dove sia
richiesta una buona maneggiabilità. L’FGS 4 è
indicata per una svariata gamma di applicazioni
industriali, fra le quali: vapore saturo e surriscaldato, agenti chimici aggressivi (eccetto ossidanti). Raccomandato nel campo petrolchimico e
termoelettrico ove sia richiesta elevata resistenza al creep.
TEMP. MAX RACCOMANDATA:
550°C (1022°F) in ambiente ossidante
700°C (1290°F) in ambiente riducente o inerte
PRESS. MAX RACCOMANDATA:
15 Mpa (150 bar; 2200 psi)
CARATTERISTICHE FISICO-MECCANICHE
spessore
mm
1.5
densità (ASTM F1315)
g/cmc 1.3
comprimibilità (ASTM)
%
40
tensione residua (BS)
MPa
32
ritorno elastico (ASTM F152)
%
≥20
resistenza a trazione (ASTM F152) MPa ≥20
contenuto di ioni di cloro (ASTM 1277) ppm <50
contenuto di ioni di fluoro
ppm <25
contenuto di zolfo
ppm <995
MISURE DISPONIBILI
lastre
mm 1500x1500
mm 1000x1000
mm 1500x1000
spessori mm 0.5-0.75-1.0-1.5-2.0-3.0
CERTIFICAZIONE Quality system accredited ISO 9001:2000
FG
FG
S4
S4
FG
FG
S4
S4
S4
FG
4
FG
F
4
GS
FG
F
4
GS
S
FG
DESCRIPTION
FGS 4 is a graphite laminate reinforced with a
flat stainless steel core.
SERVICE
FLEXIGRAF FGS 4 is recommended for high temperature, high pressure sealing applications. The inclusion of the steel reinforcing core giverise to a robust
sheet with excellent handling characteristics.
FGS 4 can be used to seal a wide range of media,
with exception of strong oxidising agents at extremes
of temperature and pressure. The soft conformable
nature of the graphite facing material makes FGS 4
suitable for sealing between worn or pitted flanges.
Typical industries where FGS 4 is used include power
generation and petrochemical.
MAXIMUM RECOMMENDED TEMP.:
Oxidising media 550°C (1022°F)
Inert or reducing media 700°C (1292°F)
MAXIMUM RECOMMENDED PRESSURE:
15 Mpa (150 bar; 2200 psi)
S4
FG
S4
FG
S4
S4
TYPICAL PHYSICAL PROPERTIES
thickness
mm
1.5
density (ASTM F1315)
g/cmc 1.3
compressibility (ASTM)
%
40
residual stress (BS)
MPa
32
recovery (ASTM F152)
%
≥20
tensile strength (ASTM F152)
MPa ≥20
leachable chlorine ion content (ASTM 1277) ppm <50
leachable fluorine ion content
ppm <25
sulphur ion content
ppm <995
AVAILABILITY
sheet size
mm 1500x1500
mm 1000x1000
mm 1500x1000
thickness range mm 0.5-0.75-1.0-1.5-2.0-3.0
CERTIFICATION Quality system accredited ISO 9001:2000
13
FMI catalogo AMIANTO 06m08.indd 13
18-06-2008 11:13:11
◆
◆
◆
Oxygen
◆
◆
◆
◆
◆
◆
◆
◆
◆
Paraffin
◆
◆
◆
◆
◆
◆
FGS
◆
◆
AFK 250
AF 240/280
AF 163/192
AF 330
◆
Ethyl Alcohol
FGS
Ethyl Acetate
AFK 250
AF 240/280
AF 163/192
AF 330
Guida alla
compatibilità chimica
Application
compatibility guide
◆
Pentachlorophenol
◆
◆
◆
◆
◆
◆
Perchloric Acid
◆
◆
◆
◆
◆
Ethyl Ether
◆
◆
◆
◆
◆
Petrol
◆
◆
◆
◆
◆
◆
FGS
◆
◆
AFK 250
◆
◆
AF 163/192
◆
◆
AF 240/280
◆
AF 330
Ethylene Glycol
Ethylene Oxide
Ethylene
◆
◆
◆
◆
◆
Phenol
◆
◆
◆
◆
Acetic Acid Glacial
◆
◆
◆
◆
◆
Ethylene Chloride
◆
◆
◆
◆
◆
Phosgene
◆
◆
◆
◆
◆
Acetone
◆
◆
◆
◆
◆
Fatty Acids
◆
◆
◆
◆
◆
Phosphoric Acid (Conc)
◆
◆
◆
◆
◆
Acetylene
◆
◆
◆
◆
◆
Ferric Chloride
◆
◆
◆
◆
◆
Phosphoric Acid (Dil)
◆
◆
◆
◆
◆
Acrylic Acid
◆
◆
◆
◆
◆
Fluorine
◆
◆
◆
◆
◆
Phosphorous
◆
◆
◆
◆
◆
Acrylonitrile
◆
◆
◆
◆
◆
Fluorosilicic Acid
◆
◆
◆
◆
◆
Phthalic Anhydride
◆
◆
◆
◆
◆
Air
◆
◆
◆
◆
◆
Formaldehyde
◆
◆
◆
◆
◆
Potassium Hydroxide
◆
◆
◆
◆
◆
Alkaline Lye
◆
◆
◆
◆
◆
Formic Acid (85%)
◆
◆
◆
◆
◆
Potassium Nitrate
◆
◆
◆
◆
◆
Aluminium Chloride
◆
◆
◆
◆
◆
Formic Acid (10%)
◆
◆
◆
◆
◆
Potassium Permanganate
◆
◆
◆
◆
◆
Ammonia Gas
◆
◆
◆
◆
◆
Freons
◆
◆
◆
◆
◆
Producer Gas
◆
◆
◆
◆
◆
Ammonia
◆
◆
◆
◆
◆
Gas Oil
◆
◆
◆
◆
◆
Pyridine
◆
◆
◆
◆
◆
Amyl Acetate
◆
◆
◆
◆
◆
Gasoline
◆
◆
◆
◆
◆
Sea water
◆
◆
◆
◆
◆
Amyl Alcohol
◆
◆
◆
◆
◆
Heating Oil
◆
◆
◆
◆
◆
Silicone Oil
◆
◆
◆
◆
◆
Aniline
◆
◆
◆
◆
◆
Hydraulic Oil (Glycol)
◆
◆
◆
◆
◆
Soda Ash
◆
◆
◆
◆
◆
Aqua-Regia
◆
◆
◆
◆
◆
Hydraulic Oil (Mineral)
◆
◆
◆
◆
◆
Sodium Bicarbonate
◆
◆
◆
◆
◆
Aviation Fuel
◆
◆
◆
◆
◆
Hydraulic Oil (Ester)
◆
◆
◆
◆
◆
Sodium Carbonate
◆
◆
◆
◆
◆
Beer
◆
◆
◆
◆
◆
Hydrazine
◆
◆
◆
◆
◆
Sodium Cyanide
◆
◆
◆
◆
◆
Benzene
◆
◆
◆
◆
◆
Hydrocarbons (Aromatic)
◆
◆
◆
◆
◆
Sodium Hydroxide (40%)
◆
◆
◆
◆
◆
Benzoyl Chloride
◆
◆
◆
◆
◆
Hydrocarbons (Aliphatic S)
◆
◆
◆
◆
◆
Sodium Hydroxide (Dil)
◆
◆
◆
◆
◆
Biphenyl
◆
◆
◆
◆
◆
Hydrocarbons (Aliphatic U)
◆
◆
◆
◆
◆
Sodium Hypochlorite
◆
◆
◆
◆
◆
Blast Furnace Gas
◆
◆
◆
◆
◆
Hydrochloric Acid (37%)
◆
◆
◆
◆
◆
Sodium Nitrate
◆
◆
◆
◆
◆
Bleach (Solution)
◆
◆
◆
◆
◆
Hydrofluoric Acid
◆
◆
◆
◆
◆
Starch
◆
◆
◆
◆
◆
Boiler Feed Water
◆
◆
◆
◆
◆
Hydrogen
◆
◆
◆
◆
◆
Steam
◆
◆
◆
◆
◆
Brine
◆
◆
◆
◆
◆
Hydrogen Chloride
◆
◆
◆
◆
◆
Steam Condensate
◆
◆
◆
◆
◆
Bromine
◆
◆
◆
◆
◆
Hydrogen Fluoride
◆
◆
◆
◆
◆
Styrene
◆
◆
◆
◆
◆
n-Butyl Acetate
◆
◆
◆
◆
◆
Hydrogen Peroxide
◆
◆
◆
◆
◆
Sulphur
◆
◆
◆
◆
◆
Calcium Chlorate
◆
◆
◆
◆
◆
Hydrogen Sulphide
◆
◆
◆
◆
◆
Sulphur Dioxide
◆
◆
◆
◆
◆
Caprolactam
◆
◆
◆
◆
◆
Isopropyl Acetate
◆
◆
◆
◆
◆
Sulphur Trioxide
◆
◆
◆
◆
◆
Carbolic Acid
◆
◆
◆
◆
◆
Isopropyl Alcohol
◆
◆
◆
◆
◆
Sulphuric Acid (Conc)
◆
◆
◆
◆
◆
Carbon Dioxide
◆
◆
◆
◆
◆
Kerosene
◆
◆
◆
◆
◆
Sulphuric Acid (Fuming)
◆
◆
◆
◆
◆
Carbon Disulphide
◆
◆
◆
◆
◆
Lime (Quick)
◆
◆
◆
◆
◆
Tar
◆
◆
◆
◆
◆
Carbon Monoxide
◆
◆
◆
◆
◆
Lubricating Oil
◆
◆
◆
◆
◆
Turpentine
◆
◆
◆
◆
◆
Carbon Tetrachloride
◆
◆
◆
◆
◆
Machine Oil
◆
◆
◆
◆
◆
Toluene
◆
◆
◆
◆
◆
Chile Saltpetre
◆
◆
◆
◆
◆
Magnesium Sulphate
◆
◆
◆
◆
◆
Towns Gas
◆
◆
◆
◆
◆
Chlorine Dry
◆
◆
◆
◆
◆
Malic Acid
◆
◆
◆
◆
◆
Transformer Oil
◆
◆
◆
◆
◆
Chlorine Wet
◆
◆
◆
◆
◆
Methane
◆
◆
◆
◆
◆
Tributyl Phosphate
◆
◆
◆
◆
◆
Chlorinated Hydrocarbons
◆
◆
◆
◆
◆
Methyl Acrylate
◆
◆
◆
◆
◆
Triethanolamine
◆
◆
◆
◆
◆
Chloroacetic Acid
◆
◆
◆
◆
◆
Methyl Alcohol
◆
◆
◆
◆
◆
Urea
◆
◆
◆
◆
◆
Chlorobenzene
◆
◆
◆
◆
◆
Methyl Isobutyl Ketone
◆
◆
◆
◆
◆
Vegetable Oil
◆
◆
◆
◆
◆
Chromic Acid
◆
◆
◆
◆
◆
Methyl Methacrylate
◆
◆
◆
◆
◆
Vinyl Acetate
◆
◆
◆
◆
◆
Copper Sulphate
◆
◆
◆
◆
◆
Methylene Chloride
◆
◆
◆
◆
◆
Vinyl Chloride
◆
◆
◆
◆
◆
Creosote
◆
◆
◆
◆
◆
Mineral Oil
◆
◆
◆
◆
◆
Vinylidene Chloride
◆
◆
◆
◆
◆
Cresol
◆
◆
◆
◆
◆
Mobiltherm
◆
◆
◆
◆
◆
Water
◆
◆
◆
◆
◆
Crude Oil
◆
◆
◆
◆
◆
Naphthalene
◆
◆
◆
◆
◆
Water Condensate
◆
◆
◆
◆
◆
Cyclohexanol
◆
◆
◆
◆
◆
Natural Gas
◆
◆
◆
◆
◆
Water Distilled
◆
◆
◆
◆
◆
1,4 Dichlorobenzene
◆
◆
◆
◆
◆
Nitric Acid (50%)
◆
◆
◆
◆
◆
Whisky
◆
◆
◆
◆
◆
Diesel Oil
◆
◆
◆
◆
◆
Nitric Acid (95%)
◆
◆
◆
◆
◆
Wine
◆
◆
◆
◆
◆
Dowtherm
◆
◆
◆
◆
◆
Nitrogen
◆
◆
◆
◆
◆
White Spirit
◆
◆
◆
◆
◆
Dye Liquor
◆
◆
◆
◆
◆
Oleum
◆
◆
◆
◆
◆
Xylene
◆
◆
◆
◆
◆
◆ = Idoneo
Suitable
◆ = In dipendenza delle condizioni di esercizio
Application Dependent
◆ = Non idoneo
Not Suitable
14
FMI catalogo AMIANTO 06m08.indd 14
18-06-2008 11:13:49
N
oi siamo qui
MILANO
BERGAM O
AUT
OST
RAD
A A4
GARDONE V. T.
MIL
ANO
ISEO
-VEN
EZIA
PALAZZOLO S/O
SALÒ
ROV ATO
PONTOGLI O
CRE
MON
A
AUT
OST
RAD
A BR
ESCIA
-CRE
MON
A
BRESCIA
DESENZANO
MONTICHIARI
MANERBIO
ORZINUOVI
VENEZIA
GHEDI
V
TO
AN
M
A
A4
Uscita
Palazzolo s/O
A4
Palazzolo s/O
exit
MILANO
A UTO ST
RA D A
A4
M IL
AN
O
EN
T
TR
A
VI
VIATARANTO
VIA BA RI
S. PANCRAZIO
VIA
FI R
EN
ZE
FMI
VENE
ZIA
O -V
EN
EZIA
VIA
VEZ
ZOL
I
ILANO
VIA M
W
e are here
FMI S.p.A. si riserva la facoltà di modificare le caratteristiche di tutti i suoi prodotti
senza obbligo alcuno. Edizione catalogo 06/2006
FMI S.p.A. reserves the right to modify characteristics of the entire companies
products, without obligation to anyone. Catalogue Edition 06/2006
13
FMI catalogo AMIANTO 06m08.indd 16
10 Q
FMI CAT 006 - REV. 1
GRAFICHE MASNERI - PALAZZOLO S/O (BS)
25036 S. Pancrazio
di Palazzolo s/O (BS)
v i a Ta r a n t o , 1 0 / 1 2
Tel. +39.030 7386033 (r.a.)