vita implant solutions - auf der Mediendatenbank der VITA Zahnfabrik

VITA IMPLANT SOLUTIONS
The Concept
VITA Farbkommunikation
VITA Farbkommunikation
VITA shade determination
VITA shade communication
VITA shade reproduction
VITA shade control
Date of issue: 10. 15
VITA shade, VITA made.
VITA CAD/CAM MATERIALS – for best solutions. Proven a million times over.
CONCEPT AND BENEFITS
VITA IMPLANT SOLUTIONS are CAD/CAM blanks for
time- and cost-efficient fabrication of implant crowns.
More information on the concept and benefits can be
found on the following pages.
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
CLINICAL EXAMPLES
CONCEPT AND BENEFITS
VITA IMPLANT SOLUTIONS INCLUDE
Implant screw
+
Crown
+
Adhesive/titanium base
+
Implant
What?
• VITA IMPLANT SOLUTIONS (IS) are blanks with an integrated interface
to an adhesive/titanium base (e.g. TiBase)
What for?
• The blanks are used for CAD/CAM fabrication of implant-supported
restorations
With what?
• They are available in three versions: VITA CAD-Temp IS, VITA ENAMIC IS
and VITA SUPRINITY IS.
CONCEPT AND BENEFITS
hig
h-s
sol trengt
utio
h
n
VITA ENAMIC IS?
• VITA ENAMIC is a hybrid ceramic with material properties to allow absorption
of masticatory forces
VITA SUPRINITY IS?
• VITA SUPRINITY is a high-strength, zirconia-reinforced glass ceramic
for effective durability
VITA CAD-Temp IS?
• VITA CAD-Temp is a composite blank for temporary restorations
SYSTEM AND COMPONENTS
VITA CAD-Temp® IS
FACTS AND EVIDENCE
temporary
solution
t
ben
r
o
abs lution
so
CLINICAL EXAMPLES
VITA ENAMIC® IS
VITA SUPRINITY® IS
BENEFITS
VITA ENAMIC® IS
Hybrid ceramic (with dual-network structure)
hi
gh
p
nt
rbe
ab s o
rec
isio
n
fast
absorbent
• absorbent material properties thanks to dentin-like elasticity
high precision
• highly accurate results in thinning margin areas
fast
• faster processing since superstructure can be seated immediately
after CAM fabrication/polishing
CONCEPT AND BENEFITS
VITA SUPRINITY® IS
Glass ceramic (zirconia-reinforced lithium silicate ceramic)
onia-reinforced
zirc
+ZrO2
Si2O
im
p
s
brilliant
• brilliant esthetics based on integrated translucency, opalescence and fluorescence
simple
• simple processing thanks to good polishing characteristics and high firing stability
high-strength
• high-strength, zirconia-reinforced glass ceramic for effective durability
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
gth
en
-str
high
le
CLINICAL EXAMPLES
Li2O
brilliant
BENEFITS
VITA CAD-Temp® IS
Composite
simple
at
ur
al
ent
effici
n
efficient
• efficient fabrication of temporary restorations thanks to a digital process
simple
• simple shaping of the emergence profile through virtual design
natural
• natural shade effect thanks to impressive light optical properties
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
CLINICAL EXAMPLES
CONCEPT AND BENEFITS
RESTORATIVE CONCEPT
Step 1
Implant placement
Step 2
Temporary
superstructure
What?
What?
VITA IMPLANT SOLUTIONS (IS)
• compatible with systems of manufacturers listed below
via TiBase interface
CAD/CAM fabrication
• temporary abutment crown (AC)
What for?
• Nobel Biocare
• Straumann
• Biomet 3i
• Astra Tech
• Friadent
• Medentika Implant
• ... and many others.
• for healing period/restoring the masticatory function
• for shaping/optimizing the emergence profile
With what?
VITA CAD-Temp® IS
CONCEPT AND BENEFITS
What?
CAD/CAM fabrication
• single-element solution
• Two-element solution
final abutment crown (AC)/IS-16 geometry
final mesostructure (MS)/IS-14 geometry
CLINICAL EXAMPLES
Step 3
Final
superstructure
What for?
for anterior superstructure: MS type + crown
With what?
FACTS AND EVIDENCE
for posterior superstructure: AC type
VITA ENAMIC® IS
or
SYSTEM AND COMPONENTS
VITA SUPRINITY® IS
CLINICAL EXAMPLES
VITA IMPLANT SOLUTIONS blanks have proven their
reliability in the clinical use. Discover examples of
clinical use on the following pages.
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
CLINICAL EXAMPLES
CONCEPT AND BENEFITS
VITA ENAMIC® IS IN THE CLINICAL USE
CASE STUDY 1
1. Implant placement, tooth 25, 26
2. Placement of Scanbody
3. Digital planning/design
2. Placement of Scanbody
3. Digital planning/design
© Associate professor Dr. Andreas Bindl
Zurich, Switzerland
CASE STUDY 2
1. Implant placement, tooth 16
© Peter Neumann, dental surgeon,
Berlin, Germany
CONCEPT AND BENEFITS
6. Result after the healing phase
CLINICAL EXAMPLES
5. Seating VITA ENAMIC IS
4. Dental technical steps (exemplary)
Polishing
Applying composite
Bonding to the base
FACTS AND EVIDENCE
Reworking
6. Result after the healing phase
SYSTEM AND COMPONENTS
5. VITA ENAMIC IS crown
FACTS AND EVIDENCE
Numerous studies confirm the special benefits of
VITA ENAMIC. Key facts and evidence can be found
on the following pages.
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
CLINICAL EXAMPLES
CONCEPT AND BENEFITS
7 REASONS FOR HIGH DURABILITY
VITA ENAMIC® IS is able to absorb masticatory forces!
Absorption of masticatory forces compared to zirconia (ZrO2)
A b s o r p ti o n o f m a s t i c a t o ry f o rc e s [ % ]
80
70
71.20 %
60
50
46.28 %
40
30
24.51 %
20
10
0
Hybrid ceramic
VITA ENAMIC
Gold alloy
glass ceramic
Material class
Modulus of
Force
elasticity [GPa] transmission (N)
Absorption of forces
(%) compared to ZrO2
Zirconia
210
641.8 N (SD 6.8)
glass ceramic
96
484.5 N (SD 5.5)
-24.51 %
Gold alloy
77
344.8 N (SD 5.7)
-46.28 %
VITA ENAMIC
hybrid ceramic
30
184.9 N (SD 3.9)
-71.20 %
Source: University of Genoa, Department for fixed and implant-prosthetic restorations, Dr. Maria Menini et al., Genoa,
Italy ([4], cf. p. 38)
Summary:
• The test shows that hybrid ceramic - compared to the comparatively stiff
zirconia - absorbs or reduces forces (70 percent).
• In addition, VITA ENAMIC - compared to glass ceramic and gold - also reveals
a higher capacity of absorption of masticatory forces.
CONCEPT AND BENEFITS
2. Applied forces are distributed more evenly!
Force-path diagram
10 0
90
CLINICAL EXAMPLES
Traditional silicate ceramic
In d e n ta ti o n f o rc e [ N]
80
70
60
50
VITA YZ
IPS e.max CAD
VITABLOCS Mark II
VITA ENAMIC
40
30
20
10
0
0
2
4
6
8
10
12
14
16
18
20
22
24
26
28
30
32
34
In d e n ta ti o n d e p th [µ m ]
Summary:
• The results indicate that occlusal forces applied are distributed over a relative
large contact surface for VITA ENAMIC.
• In addition, the force is more evenly distributed so that excess loading in
individual areas is avoided.
FACTS AND EVIDENCE
Source: Internal study VITA R&D; Kraft-Wege-Diagramm für untersuchte dentale Restaurationsmaterialien, ([1], cf. p. 38)
SYSTEM AND COMPONENTS
VITA ENAMIC hybrid ceramic
7 REASONS FOR HIGH DURABILITY
3. VITA ENAMIC® superstructures feature superior load capacity!
Static fracture load of implant crowns made of VITA EMAMIC IS
1200
F r a c tu re l o a d [ N]
1000
800
600
400
200
0
VITA ENAMIC IS L
average masticatory
force1
Source: Internal study: VITA R&D; Bruchlast VITA ENAMIC IS Kronen auf L-TiBase Klebebasen und Straumann Bone
Level Implantatsystem, ([1], cf. p. 38)
Summary:
• Implant-supported molar crowns made from VITA ENAMIC withstand an
average load of approx. 926 N in this test.
• Compared to the average maximum masticatory force of approx. 490 N1,
the molar crowns tested reached a higher level of load capacity.
1Körber K, Ludwig K (1983). Maximale Kaukraft als Berechnungsfaktor zahntechnischer Konstruktionen.
Dent-Labor XXXI, Heft 1/83: 55 – 60.
CONCEPT AND BENEFITS
4. VITA ENAMIC® achieves a high level of dynamic loading!
CLINICAL EXAMPLES
700
600
500
400
300
200
100
0
VITA ENAMIC IS L
Source: Internal study: VITA R&D; Dynamische Bruchlast VITA ENAMIC IS Kronen auf L-TiBase Klebebasen und Straumann Bone
Level Implantatsystem, ([1], cf. p. 38)
Summary:
• In this test a level of permanent loading of 648 N (100 % survival rate) was achieved
for implant-supported molar crowns made of VITA ENAMIC IS at 2 million cycles.
FACTS AND EVIDENCE
approx. level of permanent loading of ZrO2 abutments according to literature sources 1 – 3
• References for dynamic load tests indicate a level of permanent loading of
approx. 400 N for zirconia abutments on implants.*
* Note: Depending on the test setup, number of cycles and type of implant, test results vary and can only
be compared to one another to a limited extent.
1 Gehrke et al.; Zirconium implant abutments: fracture strength and influence of cyclic loading on
retaining-screw loosening; Quintessence Int. 2006 Jan; 37(1):19-26.
2 Mitsias et al.; Reliability and fatigue damage modes of zirconia and titanium abutments;
Int J Prosthodont. 2010 Jan-Feb; 23(1):56-9.
3 Jiménez-Melendo et al.; Mechanical behavior of single-layer ceramized zirconia abutments for dental
implant prosthetic rehabilitation; J Clin Exp Dent. 2014 Dec 1;6(5):e485-90
SYSTEM AND COMPONENTS
L e v e l o f p e r m a n e n t l o a d i n g a t 2 m i l l i o n c y c l e s [ N]
Dynamic fracture load of implant crowns made of VITA ENAMIC IS
7 REASONS FOR HIGH DURABILITY
5. VITA ENAMIC® features a damage-tolerant dual-network structure!
Crack formation
plastic deformation
VITA ENAMIC hybrid ceramic
Magnification
Traditional silicate ceramic
Source: Internal study VITA R&D; Querschnitt der Bruchfläche nach Vorschädigung mit einer Wolframcarbid-Kugel, ([1],
cf. p. 38)
Summary:
• Following prior damage and loading, VITA ENAMIC reveals plastic deformation
and, as a result, a certain level of damage tolerance in the test.
• A relatively brittle and stiff material, such as traditional silicate ceramic,
reveals cracks in this test following prior damage and loading.
CONCEPT AND BENEFITS
6. In tests, VITA ENAMIC® demonstrates good abrasion resistance.
Abrasion tests
250
CLINICAL EXAMPLES
150
100
50
0
Material abrasion
IPS e. max CAD
Paradigm MZ 100
Antagonist abrasion
Source: University of Regensburg, Faculty of Medicine, Polyclinic for Dental Prosthetics, Prof. Martin Rosentritt,
Technical and Scientific Documentation. VITA ENAMIC, VITA Zahnfabrik, Bad Säckingen, ([3], cf. p. 38).
Summary:
• In tests, VITA ENAMIC demonstrates high abrasion resistance comparable
to that of proven dental ceramics.
FACTS AND EVIDENCE
VITA ENAMIC
• These results can be achieved since the hybrid ceramic features
a dominant ceramic network.
SYSTEM AND COMPONENTS
A b r a si o n [ µ m ]
200
7 REASONS FOR HIGH DURABILITY
7. Studies indicate good stability!
Survival rate of VITA ENAMIC implant-supported crowns
100
98.7 %
95
after 45.6 months
90
Su r v i va l ra t e [ % ]
85
80
75
70
65
60
55
50
1
5
10
15
20
25
30
35
40
45
50
M o n th s
Source: Multicenter clinical observational study; VITA Application Technology and VITA Product Management
departments in cooperation with pilot users (= 11 practicing dentists, Germany/Austria/Switzerland), as of:
11.2014, ([2], cf. p. 38)
Summary:
• A survival rate of 98.7 % was determined for VITA ENAMIC implant crowns
after a max. observation period of 45.6 months.
• A total of 60 VITA ENAMIC implant crowns were inserted and observed.
The average wearing period of the implant crowns in this study was 23.1 months
(as of: 11.2014).
CONCEPT AND BENEFITS
3 REASONS FOR EFFICIENT PROCESSING
+ Polishing/bonding: approx. 10 minutes = approx. 20 minutes
• As a result, after CAM processing over a few minutes, the polished
restoration can be directly seated.
FACTS AND EVIDENCE
Summary:
• VITA ENAMIC IS superstructures can be fabricated in a way to save
a tremendous amount of time and costs (e.g. no firing).
SYSTEM AND COMPONENTS
CAM fabrication: approx. 10 minutes
CLINICAL EXAMPLES
1. Fabricating implant crowns in a short time with VITA ENAMIC® IS!
3 REASONS FOR EFFICIENT PROCESSING
approx. 276 µm
approx. 87.5 µm
2. VITA ENAMIC®: Accurate CAM results for precise marginal fit!
IPS e.max CAD
Magnification
VITA ENAMIC
Source: Internal study VITA R&D, top view of 30° wedge, manufactured with Sirona MC XL system, 200 x magnification,
([1], cf. p. 38)
Summary:
• VITA ENAMIC IS can be processed with incredible precision using CAD/CAM
technology, particularly in thin marginal areas.
• As a result, exact marginal fit can be achieved between the superstructure and
the mesostructure or the adhesive/titanium base.
CONCEPT AND BENEFITS
3. VITA ENAMIC® can be easily processed!
• VITA ENAMIC IS ensures that if a screw becomes loose, for example,
the integrated interface provides easy access to the screw canal.
CLINICAL EXAMPLES
Easy access
VITA ENAMIC IS: Simple2
SYSTEM AND COMPONENTS
• The screw canal can then be simply and reliably sealed again using
composites.
FACTS AND EVIDENCE
Simple sealing
2 REASONS FOR A SIGNIFICANT ESTHETIC POTENTIAL
1. VITA ENAMIC® provides excellent photo-optical properties!
Zirconia solution, non-colored
Tooth-colored hybrid ceramic solution
versus
Summary:
• VITA ENAMIC IS is a tooth-colored hybrid ceramic that provides excellent
photo-optical properties.
• As a result, dental practices and laboratories can fabricate highly-esthetic
superstructures using this material solution.
CONCEPT AND BENEFITS
2. Numerous options for characterization and surface texturing!
• When fabricating VITA SUPRINITY restorations, VITA AKZENT Plus stains
and VITA VM 11 veneering material are used to reproduce individual
characteristic features.
CLINICAL EXAMPLES
• VITA ENAMIC Stains and VITA VM LC/VM LC flow provide numerous
options for shade characterization and individualization of implantsupported hybrid ceramic restorations.
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
• To create a surface texture and achieve a high level of gloss in implantsupported restorations, matched polishing instruments contained in the
VITA ENAMIC or VITA SUPRINITY polishing sets are available.
SYSTEM AND COMPONENTS
The VITA IMPLANT SOLUTIONS restorative concept
is comprised special blanks and components.
You can find an overview in this publication.
SYSTEM AND COMPONENTS
FACTS AND EVIDENCE
CLINICAL EXAMPLES
CONCEPT AND BENEFITS
MATERIALS AND GEOMETRIES
VITA CAD-Temp® IS (temporary solution)
Abutment crown (AC)
VITA CAD-Temp IS-16
VITA IMPLANT SOLUTIONS (IS)
VITA ENAMIC® IS (final solution)
Mesostructure (MS)
VITA ENAMIC IS-14
Abutment crown (AC)
VITA ENAMIC IS-16
VITA SUPRINITY® IS (final solution)
Mesostructure (MS)
VITA SUPRINITY IS-14
Abutment crown (AC)
VITA SUPRINITY IS-16
The suitable type for a variety of requirements!
+
=
+
Temporary and final solutions cleverly combined.
=
CONCEPT AND BENEFITS
SHADES AND TYPES
Available shades:
• VITA ENAMIC IS-14 (MS type) with S- or L-interface in:
1M1-T, 1M2-T, 2M2-T, 3M2-T, 4M2-T
CLINICAL EXAMPLES
• VITA ENAMIC IS-16 (AC type) with S- or L-interface in:
1M1-HT, 1M2-HT, 2M2-HT, 3M2-HT, 4M2-HT
• VITA SUPRINITY IS-14 (MS type) with S- or L-interface in*:
A1-T, A2-T, A3-T, A3.5-T
0M1-T, 1M1-T, 1M2-T, 2M2-T, 3M2-T, 4M2-T
• VITA SUPRINITY IS-16 (AC type ) with S- or L-interface in*:
A1-HT, A2-HT, A3-HT, A3.5-HT
0M1-HT, 1M1-HT, 1M2-HT, 2M2-HT, 3M2-HT, 4M2-HT
• VITA CAD-Temp IS-16 (AC type) with S- or L-interface in:
1M2T, 2M2T, 3M2T
IS-14: 18 x 14 x 12 (for mesostructures)
Note: with an integrated S- or L-interface for each
geometry size
IS-16
IS-16: 18 x 16 x 18 (for abutment crowns)
*) The product information on VITA SUPRINITY IS is provisional; the blanks will probably be available at the end of the year.
SYSTEM AND COMPONENTS
IS-14
FACTS AND EVIDENCE
Available geometries:
PERFECTLY MATCHED SYSTEM SOLUTIONS!
CAD/CAM systems?
VITA offers VITA IMPLANT SOLUTIONS blanks with a specific holder system
for the CAD/CAM system:
• CEREC/inLab (Sirona Dental GmbH) from software version 4.4 (CEREC)
or software
15.0 (inLab)*
Implant systems?
VITA IMPLANT SOLUTIONS are compatible** with implant systems from
the manufacturers listed below via the integrated interface for the adhesive/
titanium base (TiBase, Sirona Dental GmbH):
• Nobel Biocare
• Straumann
• Astra Tech
• Friadent
• Zimmer
• Medentika Implant
• CAMLOG
• Biomet 3i
*) VITA SUPRINITY IS will be integrated in a higher software version.
**) A comprehensive, up-to-date overview of the implant systems compatible with TiBase is available at:
http://www.sirona.com
Shade
determination
• For digital shade determination, use VITA Easyshade V, and for
visual shade determination the VITA Linearguide 3D-MASTER
or VITA classical A1–D4, for example.
CAD/CAM
Fabrication
• For CAD/CAM fabrication of superstructures, VITA offers you
composite, hybrid ceramic and glass blanks – simply select
the best material solution for your individual requirements.
Shade
modification*
Firing*
• For glass ceramics, use VITA AKZENT Plus stains and
VITA VM 11 veneering material. Use VITA ENAMIC Stains
for the hybrid ceramic and VITA VM LC for individualization.
• Glaze, stains and/or dentine and crystallization firing are best
carried out with the VITA VACUMAT 6000 M.
• Note: When using hybrid ceramic/composite, firing must not
be carried out.
Polishing
• For VITA glass and hybrid ceramics, VITA SUPRINITY /
VITA ENAMIC polishing sets should ideally be used.
Bonding
• When bonding VITA glass and hybrid ceramics,
you can use a bonding system recommended by VITA.
*Note: The feldspar and hybrid ceramic materials can be seated directly after milling and polishing.
Crystallization firing is mandatory for the glass ceramic.
Note: The VITA product solutions mentioned above are registered trademarks of VITA Zahnfabrik.
Firing is not carried out.
WE WILL BE GLAD TO HELP
More information about the products and processing
is available at www.vita-zahnfabrik.com/cadcam
and from the hotline/mail contacts below.
Hotline Sales Support
Phone +49 (0)7761 / 562-884, Fax +49 (0)7761 / 562-299
8 a.m. to 5 p.m.
Mr. Udo Wolfner and his team (Internal Sales Department)
will be glad to assist you when recording orders or if
you have questions about the delivery, product data and
advertising media.
Mail contact
You can email your questions and requests to
[email protected]!
Technical Hotline
Phone +49 (0)7761 / 562-222, Fax +49 (0)7761 / 562-446
8 a.m. to 5 p.m.
If you have technical questions concerning the
VITA CAD/CAM product solutions, you can contact our
technical specialists Mr. Ralf Mehlin or Mr. Daniel Schneider.
VITA CAD/CAM MATERIALS – for best solutions. Proven a million times over.
Best solutions for temporary
restorations/auxiliaries
Best solutions
for substructures/
fully anatomical bridges
Best solutions for
single-tooth restorations
VITA CAD/CAM
MATERIALS
VITA SUPRINITY IS
VITA ENAMIC IS
®
®
high
-s
solu trengt
tion h
ent
orb ion
s
b
a olut
s
temporary
solution
VITA CAD-Temp IS
®
Best solutions for implant-supported
restorations
VITA IMPLANT SOLUTIONS (IS) are blanks comprised of hybrid
ceramic, glass ceramic or composite for the CAD/CAM fabrication
of implant-supported dental restorations. They feature an integrated
interface for an adhesive / titanium base (e.g. TiBase).
Bibliography
1.
Internal studies, VITA R&D:
VITA Zahnfabrik H. Rauter GmbH & Co. KG
Ressort Forschung und Entwicklung
Spitalgasse 3, 79713 Bad Säckingen
With the unique VITA SYSTEM 3D-MASTER, all natural
tooth shades can be systematically determined and perfectly reproduced.
Dr.-Ing. Andrea Coldea, Materialentwicklung F&E, Bad Säckingen
Prof. Dr. Dr. Jens Fischer, Ressortleiter F&E, Bad Säckingen
Date of issue: 08/2015
For detailed test data see
Technical and scientific publication - VITA ENAMIC;
Download at www.vita-zahnfabrik.com/cadcam
Clinical application study:
VITA Anwendungstechnik und Produktmanagement:
VITA Zahnfabrik H. Rauter GmbH & Co. KG
Ressort Vertrieb
Spitalgasse 3, 79713 Bad Säckingen
Claus Pukropp, Leiter Technisches Marketing, Bad Säckingen
Andreas Buchheimer, Leiter Anwendungstechnik, Bad Säckingen
Date of issue: 11/2014
3.
Priv.-Doz. Dr.-Ing. Martin Rosentritt, Head of Research Division,
University Clinic,
Regensburg, Polyclinic for Dental Prosthetics, Regensburg, 2011
4.
Dr. Maria Menini, Department for fixed and implant-prosthetic restorations,
University of Genoa, Italy, 01/2015
Please note: Our products must be used in accordance with the instructions for use.
We accept no liability for any damage resulting from incorrect handling or usage. The
user is furthermore obliged to check the product before use with regard to its suitability for the intended area of application. We cannot accept any liability if the product is used in conjunction with materials and equipment from other manufacturers
that are not compatible or not authorized for use with our product. Furthermore, our
liability for the accuracy of this information is independent of the legal basis and, in
as far as legally permissible, shall always be limited to the value as invoiced of the
goods supplied, excluding value-added tax. In particular, as far as legally permissible,
we do not assume any liability for loss of earnings, indirect damages, ensuing
damages or for third-party claims against the purchaser. Claims for damages based
on fault liability (culpa in contrahendo, breach of contract, unlawful acts, etc.) can
only be made in the case of intent or gross negligence. The VITA Modulbox is not
necessarily a component of the product.
Date of issue of this information: 10.15
After the publication of these information for use any previous versions become
obsolete. The current version can be found at www.vita-zahnfabrik.com
VITA Zahnfabrik has been certified in accordance to the Medical Device Directive
:
and the following products bear the CE mark
VITA ENAMIC® IS, VITA SUPRINITY® IS, VITAVM®11, VITA AKZENT® Plus,
VITA CAD-Temp® IS, VITAVM®LC
The products/systems of other manufacturers mentioned in this document are
registered trademarks of the respective manufacturers.
10149 E - 1015 (X.) S - Version (01)
2.
VITA Zahnfabrik H. Rauter GmbH & Co.KG
Postfach 1338 · D-79704 Bad Säckingen · Germany
Tel. +49(0)7761/562-0 · Fax +49(0)7761/562-299
Hotline: Tel. +49(0)7761/562-222 · Fax +49(0)7761/562-446
www.vita-zahnfabrik.com · [email protected]
facebook.com/vita.zahnfabrik