measuring and testing ElektroPhysik Mefigerate fur

measuring and testing
?§
ElektroPhysik
Mefigerate fur Oberflachentechnik Surface Testing Instruments
^T
MiniTest®
4100/3100/2100/1100
Non-destructive coating thickness
measurement
MiniTest® 4100/3100/2100/1100 (DIN, BS, ASTM, ISO)
Electronic coating thickness gauges for all non-magnetic coatings on steel
and all insulating coatings on non-ferrous metals.
MiniTest® 600
• Dual probe to measure both on ferrous and
non-ferrous substrates
• Any number of probes can be usedffor measurements from lum to 100 mm)
• 99 calibration memories
• Memory capacity of 10,000 readings, 500 groups of readings
• Backlit display
• Date and time of measurements are stored
• Audio signals for out-of-limit readings
• Interface for PC and printer (RS 232)
• Different statistical data processing methods
MiniTest 600F-600N-600FN (DIN, BS, ASTM, ISO)
Coating thickness measurement gauge for the non-destructive coating
thickness measurement.
MiniTest 600F for all galvanic layers, lacquer and paint coatings on steel
MiniTest 600N for anodising, lacquer, paint etc. on non ferrous metals
MiniTest 600FN Universal gauge to measure on steel and non-ferrous
metals.
Ranges: 0 ... 3000 microns (F) resp. 0 ... 2000 microns (N)
eXacto®
MiniPrint
Data printer; provides on-the-spot or later printout of readings, statistical
values and histograms (no photo).
eXacto® (DIN, BS, ASTM, ISO)
The ideal gauge for mobile coating thickness measurement
• For non-magnetic coatings on steel and all insulating coatings on
non-ferrous metals
• With integrated probe for one-hand operation
• User-friendly menu operation
• Monitoring of tolerances through limit setting
• Statistical evaluation
• Measuring range: 0...2000 um for F, N, FN probes
• Data memory for up to 90 single readings
• RS 232 interface for connecting to MiniPrint or PC
MikroTesf* automatic
MikroTest" automatic
magnetic coating thickness gauge, using the magnetic attraction principle
for non-destructive measurement of:
•
•
•
•
•
all non-magnetic coatings on steel
electroplated nickel coatings on non-ferrous substrates
electroplated nickel coatings applied directly to a steel base
coating thickness standards available for all measuring ranges
no power supply required, completely automatic testing procedure,
measuring ranges:
0... 100 um, 0...1000 um,
0.2...3 mm, 0.5...5 mm,
2.5...10 mm, 7.5...20 mm.
PenTest® and
MiniPen
Non-destructive coating thickness
measurement
PenTest "/ MiniPen
Magnetic coating thickness gauges using the magnetic attraction principle, for the non-destructive, fast and simple measurement of all non-ferrous coatings such as paint, plastics and enamel on steel. No power supply
required.
PenTest
With patented HOLD mechanism. Measuring principle according to DIN
EN ISO 2176. Measuring range: 25...700 um. International patents.
QuintSonic
MiniPen
Suitable pull-off gauge for both, industrial and consumers application.
Measuring range: 50...500 pm.
SurfaTest (no photo)
Wet film coating thickness gauge
For use on freshly-painted wet surfaces - an indispensable measuring tool
for all paint shops. Measuring range: 25...800 urn.
QuintSonic
Ultrasonic coating thickness measuring gauge for the non-destructive
measurement of paint, varnish, plastics, etc.
New: measurement of a multi-layer system in
only one measuring process
Rocky
Measuring range: single-layer: 10 ... 500 microns
multi-layer: max. 500 microns
Rocky
SurTest
Portable hardness tester for the universal use for measurement in the
laboratory or in workshops. It is easy to use with a very low tolerance of
+/- 0,8 %. There are different impact devices available for different applications. Documentation is possible with a built-in printer. The hardness
can be indicated in Rockwell С (HRC), Rockwell В (HRB), Rockwell A
(HRA), Vickers (HV), Brinell (HB), Shore (HS) and Leeb (HL). The gauge
measures the U.T.S.
Impact (no photo)
Low-cost hardness tester with integrated impact body for standard
applications. Technical data: As for Rocky, but without printer.
Roughness Testing
SurTest
A small, handy pocket gauge for measuring surface roughness Ra or Rz.
Simply place the SurTest in position, press the button and within seconds
this electronic gauge gives a digital display of the readings. For use on the
production line, in the workshop and the laboratory.
GalvanoTest®
Destructive coating thickness
measurement
The GalvanoTest is a universal coating thickness gauge which works
on the anodic dissolution principle (DIN S095S, ISO 2177). It can be used
for virtually all electroplated single- coat and multi-coat systems such as
chrome, nickel, cadmium, copper, brass, silver, tin, zinc on metal and
non-metal substrates. The standard gauge version can test up to 70 coating/base combinations directly without any accessories.
Measuring range: O.OS...approx. 100 um, digital display, test areas:
0.25 mm', 1 mm2, 4 mm2.
Special accessories required for measurement on wire. The gauge is
supplied with interfaces for connection to a PC, printer and xt recorder.
Registered design
Paint Borer
PIG
Paint Borer
A universal gauge for the precise thickness measurement of all coatings on
any coatable base, e. g. varnish and paint on wood, plastics, metal, etc.
Test principle: a conical bore is taken of the test coating; microscopic measurement procedure (similar to wedge-cut method).
Measuring range: 2...200 um, 3...300 um, 5...500 um, 10...1000 um.
PIG (Paint Inspection Gauge)
(DIN 50986) a universal coating thickness gauge which uses the wedgecut method to test the thickness of all coatings on metal, wood and
plastic. Also recommended for the measurement of single layers in multicoat systems. Measuring range: 2...200 um, 5...500 urn, 10...1000 um,
20...2000 um.
StratoTest® 4100
Non-destructive road surface thickness
measurement
.!
StratoTest™ gauge for non-destructive measurement of the thickness of
bituminous road surfaces and other insulating coatings. The gauge works
on the eddy current principle.
• gauge and probe easily manoeuvrable
• measuring range 0...30 cm, optional (0...10 cm, 0...40 cm, 0... 100 cm)
\ • digital display
• memory for up to 6000 readings
• a printer can be connected to print out readings and statistics plus
histogram
• interface for evaluation of results on a PC
Porosity detection
PoroTest 3, 15, 35
Versatile pore detectors for locating pin holes and flaws in insulating coatings such as paint, plastic, enamel, bitumen etc. on all metals and also on
concrete (DIN 55670). Test principle: flashover with DC or pulsed high
voltage. Test voltages: 500...3,000 V, 2,000...15,000 V, 10,000...35,000 V;
inbuilt rechargeable battery ensures full operating flexibility.
Registered design
Mini lest FH4100
Minilcst ' FH2100
Wall thickness measurement
MiniTest® FH 4100/FH 2100
Wall thickness gauge for accurate measurement of the wall thickness of
non-magnetic materials. A magnetic probe is placed on one side of the
material to be measured and a target steel ball follows the probe on the
other side.
•
•
•
•
•
•
7 measurements per second
500 batches available for storing 10,000 readings
Illuminated display (optional)
Date and time of measurements are stored
Interface RS 232 bi-directional for data transfer
Different statistical data processing methods
MiniTest®400W
MiniTest®400W
Ultrasonic wall thickness measuring gauge for the quick, non-destructive
measurement of wall thickness of metal, plastic, glass etc. Also to detect
pitting and corrosion on the inaccessible side. Range: 1 ... 500 mm (resolution 0,01 mm), ambient temperature: -10"C ... +55°C
RecoTest
Thickness measurement,,
RecoTest
Thickness measuring gauge to measure reinforced and prestressed
concrete cover
Newly developed universal probe
• for depth measurement (0 ... 150 mm)
• for spot measurement (0 ... 80 mm)
• for determination of rebar diameter
PicoGloss MC
ent
Gtosj ffieasurejne
PicoGloss MC (ISO, ASTM, DIN, BS, JIS, NFT)
Microprocessor controlled gloss meter for measurement of gloss on level
surfaces using the principle of a reflectometer.
• Gloss measurement in the range 0.0.. 150.0 gloss units
• Mirror gloss measurement from 150 - 1999 gloss units
with autoranging facility
• Automatic calibration
• Measuring data memory for 500 measured values in up to 99 batches
• RS 232 Interface for data transmission and control of the instrument via
PC with software PICOSOFT
Continuous Thickness Measurement
CTM-3000 / CTM 2000
Notes
Thickness measuring system suitable
for all non-magnetic
materials such as
• vulcanised and unvulcanised rubber
• coated and uncoated textiles
• PET, PVC, PUR, non-woven,
pastry materials, felt, ceramics, etc.
Measuring capacity: 0,01 ... 10 mm in
two measuring ranges
Tolerance: 1% of reading
The measurement is unaffected
by variations in density, humidity,
vibrations and temperature.
Continuous Puihole Detection (CPD)
Pinhole detection system for
detection of holes, tears and slits
in all electric insulating materials
such as
• PUR, PET, PVC, foils and laminates
Material thickness: 0,03 ... 8 mm,
Material speed: max. 200 m/min,
Contacting or non-contacting
testing is available
• Holes smaller than 50 um
• Nearly 100% testing in machine
direction
ElektroPhysik
Meftgerate fur Oberflachentechnik Surface Testing insti
ElektroPhysik
Dr. Steingroever GmbH&Co.KG
Pasteurstr. 15
D-50735 Koln
Tel. (0221)75204-0
Fax (02 21) 7 52 04-67
www.elektrophysik.com
[email protected]
ElektroPhysik USA
770 West Algonquin Rd.
Arlington Heights IL 60005
Phone (8 47) 4 37-6616