ROCKWOOL RockTech S Series Datasheet

INDUSTRIAL AND TECHNICAL
ROCKWOOL® productSHEET
200 305-02/14_V1 (en)
RockTech S
(Slab) Series
General Product Information
ROCKWOOL stone wool products are made of basalt, a volcanic stone.
ROCKWOOL stone wool products are non-combustible with a
ROCKWOOL stone wool is inorganic and contains no nutri-
melting point of approximately 1000°C. They are particularly
tious substance. Therefore it will not be attacked by microor-
suitable for thermal insulation, fire protection and sound re-
ganisms. Stone wool will not rot and does not attract vermin.
duction/absorption.
No CFCs, HFCs, HCFCs or asbestos are used in the manufacture of ROCKWOOL stone wool products.
INDUSTRIAL AND TECHNICAL
ROCKWOOL® productSHEET
200 305-02/14_V1 (en)
RockTech S (Slab)
Common applications
Specially formulated RockTech S850 product is designated to
be used for maximum service temperature of up to 850°C. The
RockTech S is particularly suited to meet the specification
optimum thickness to be used can be calculated with the use of
requirements of thermal insulation, fire protection and
sophisticated thermal insulation software available in ROCK-
sound attenuation of both flat and slightly curved surfaces of
WOOL with the selected RockTech S series product.
tanks, vessels, boilers and ducts. The fibre structure of
RockTech S provides the product with great dimensional sta-
Basic installation guideline
bility and pressure resistance.
RockTech S can be easily cut to required shape, length and
RockTech S is normally used to insulate and achieve the de-
width with a use of a handsaw or a sharp knife. RockTech S is
sired surface temperature and minimize the heat loss from
securely fastened to the equipment to be insulated with the
equipment, thus providing energy saving to the overall process.
use of insulation pins which is either mechanically fastened
INDUSTRIAL AND TECHNICAL
ROCKWOOL® productSHEET
200 305-02/14_V1 (en)
RockTech S (Slab)
7
1
2
3
4
1
6
5
RockTech S
Stainless steel
bands (weather proofing)
2
3 Stainless steel bands
4
Support ring
5
Protrusion
6
Cladding
Roof/wall connection
7
or spot welded onto the surface of the equipment. The edges
lengthwise and crosswise joints with a self-adhesive alu-
of each slab should be butt jointed closely together. All steel
minum tape (≥ 75mm width). When the insulating equipment
components or equipment to be insulated which is exposed
is colder than the ambient temperature, and there is a risk of
to a corrosive environment should be cleaned, de-greased
condensation, the insulation should be provided with a va-
and coated with a protective finish before insulation is in-
pour barrier.
stalled onto it.
Packaging and storage
The insulation should be finished with metal cladding i.e. aluminum or other approved cladding material. Both lengthwise
RockTech S is shrink-wrapped in polyethylene sheets for ease
and circular joints of the cladding are fastened with sheet
of handling, transportation, storage and identification. Prod-
metal screws or rivets. All the connections within the clad-
ucts should be stored indoors or under a waterproof covering.
ding should be made watertight using suitable sealant. In the
Ensure the insulation is not in direct contact with the floor;
event aluminum foil faced finishing is preferred, finished
otherwise it may become wet as a result of ground moisture.
INDUSTRIAL AND TECHNICAL
ROCKWOOL® productSHEET
200 305-02/14_V1 (en)
RockTech S (Slab)
Technical Parameters
Density
Length x Width
Thermal conductivity
50 0C
100 0C
150 0C
200 0C
250 0C
300 0C
350 0C
400 0C
450 0C
Hot surface performance
Linear shrinkage, max % at
maximum use temperature
Compressive strength
Surface burning characteristic
FSI
SD
Chloride content *
Water absorption
(partial immersion)
Water vapor sorption
Corrosion to stainless steel
Health & Safety:
Odor emission
Fungi resistance
Compliance to standard
S350
60kg/m3
S450
S650
80kg/m3
100kg/m3
1200mm x 600mm
0.037W/mK
0.045W/mK
0.053W/mK
0.060W/mK
0.038W/mK
0.045W/mK
0.054W/mK
0.061W/mK
0.074W/mK
0.038W/mK
0.044W/mK
0.050W/mK
0.057W/mK
0.065W/mK
0.075W/mK
0.088W/mK
350 0C
0%
450 0C
0.2%
650 0C
0.5%
S850
110kg/m3
0.038W/mK
0.045W/mK
0.054W/mK
0.060W/mK
0.072W/mK
0.083W/mK
0.099W/mK
0.115W/mK
0.131W/mK
850 0C
0.02%
Standards
EN1602
EN882
ASTM C177
ASTM C411/ ASTM C447
ASTM C356
EN826
ASTM E84
Min 4 kPa, Max 30 kPa at 10% relative deformation
0
Max 30
‹=10ppm
Min 0.12kg/m2, Max 0.30kg/m2
ASTM C871
BSEN1609
0.040% by weight 0.042% by weight 0.050% by weight 0.031% by weight
Conforms to the stainless steel corrosion specification as per
ASTM C692 and C871 test method
ASTM C1104
ASTM C692/ ASTM C795
No perceptible odour present
Does not encourage growth of fungi
ASTM C612 “Standard specification for mineral fibre board and
board thermal insulation” Type IA to IVB
ASTM C665-06
ASTM C1338
*Chloride content varies between ROCKWOOL factories; please consult your local sales or technical representatives for the exact value.
www.rockwoolasia.com
Rockwool Malaysia
Sdn Bhd
Lot 4, Solok Waja 1
Bukit Raja Industrial Estate
41050 Klang, Selangor
Malaysia
T (+60) 3 3341 3444
F (+60) 3 3342 7290
Rockwool Malaysia
Sdn Bhd
175 A&B
Kawasan Perindustrian
Air Keroh, Jalan Lingkungan
Usaha, 75450 Melaka
Malaysia
T (+60) 6 233 2010
F (+60) 6 233 2012
Rockwool (Thailand) Limited
Hemaraj Eastern Industrial
Estate (Map Ta Phut)
1 Soi G 2, Pakornsongkrohraj
Road, Huaypong, Muang
Rayong 21150
Thailand
T (+66) 3868 5110
F (+66) 3868 4938
Disclaimer: The information contained in this
data sheet is believed to be correct at the date
of publication. ROCKWOOL does not accept
responsibility for the consequences of using
RockTech S in applications different from those
described above.