cenia stone - Piedra Natural, Piedra Cenia, Inmar

CENIA STONE
www.inmar-group.com
Our company boasts over 35 years of experience in treating
and processing Natural Stone for use in the restoration and
renovation of buildings and architectural structures, such as
the restorations of the PRADO MUSEUM and the CATHEDRAL
OF ALCALA DE HENARES, both of which used our materials,
as well as other projects featured below:
SOME IMPORTANT PROJECTS AROUND THE WORLD:
• SUPREME EDUCATION COUNCIL HEADQUARTER. (DOHA, QATAR)
• F.C.BARCELONA STADIUM “CAMP NOU”. (BARCELONA, SPAIN)
• L’ILLA SHOPPING CENTER. (BARCELONA, SPAIN)
• PRADO MUSEUM. (MADRID, SPAIN)
• ALNAKHIL PALACE (JEDADHH, SAUDI ARABIA)
• SHERATON HOTEL (MAUI, HAWAI, USA)
• AL AIN UNIVERSITY. (ABU DHABI)
• “MIDSUMMER PLACE” SHOPPING CENTER (MILTON KEYNES, UNITED KINGDOM)
• HELEN AND MARTIN KIMMEL BUILDING. NEW YOR UNIVERSITY (NEW YORK, USA)
• KURSSAL EXHIBITION CENTER. (S. SEBASTIAN, SPAIN)
• HILTON HOTEL (DAKAR)
• SPANISH OLYMPIC HEADQUARTER. (MADRID, SPAIN)
• SWISS BANK CORPORATION (BASEL, SWITZERLAND)
• “CON EDISON” BUILDING ( NEW YORK, USA)
• LA MORALEJA SHOPPING CENTER. (MADRID, SPAIN)
• PAUL SABATIER UNIVERSITY (TOULOUSE, FRANCE)
• LILLY LABORATORIES HEADQUARTER. (MADRID, SPAIN)
• NESTLE BUILDING (VEVEY, SWITZERLAND)
• CITADINES RAMBLE HOTEL. (BARCELONA, SPAIN)
• SAVOY HOTEL (CANNES, FRANCE)
• “MARSEILLE ROADS“ OPERA .(FRANCE)
• SEVILLA OLYMPIC STADIUM. (SEVILLA, SPAIN)
• STADE DE FRANCE (SAINT DENIS, FRANCE)
• PROMENADE DES BARQUES COURS MIRABEAU (NARBONNE, FRANCE)
• AHMED BEY SQUARE (CONSTANTINE, ALGERIA)
• HOTEL “CA XICA” (IBIZA, SPAIN)
• KINGS COUNTY COURTHOUSE (SAN LEANDRO, CALIFORNIA, USA)
• REMODELLING OF SPANISH NAVY PROMENADE (CEUTA, SPAIN)
The INMAR Group has its own quarries of Cenia Cream (limestone) and has been
granted the administrative licence from the town of Ulldecona (Tarragona), with
important reserves to guarantee a constant supply of raw materials in response
to increases in demand for both new-build and the upkeep of finished buildings.
Our materials can be produced to any size and thickness.
• Tiles of 305 x 305 x 10 mm, 457 x 457 x 10 mm and 410 x 410 x 10 mm.
• Standard tiles of 1.5 cm to 3 cm.
• Standard tiles of: 60x40 x2 / 60x30x2 / 40x40x2.
• Standard and large cladding.
2
CENIA STONE
• Street paving from 3 cm to 10 cm.
• Special thicknesses for architectural projects.
All the above products can be supplied in different finishes depending on their
final use:
Interiors: Honed, Polished and Aged.
Exteriors: Cut, Sandblasted, Honed, Flamed and Bush-Hammered.
Each of these finishes is obtained by a process involving state of the art machinery
and technology to guarantee the optimum quality of all our products.
CENIA stone was formed in the Lower/Early Cretaceous Period. It falls within the category of sedimentary limestone that
has been recrystallized by metamorphosis and is classifiable as marble. Its technical properties make it ideal for both
interior and exterior use in the following finishes:
Grinded Cenia
Polished Cenia
Aged Cenia
TECHNICAL CARACTHERISTICS
Petrographic study (petrographic definition)
Dolomitic
limestone
Flexing resistance (minimum expected value)
9.6 Mpa
Flexing resistance (minimum expected /average
value after 48 frost/thaw cycles)
Flamed Cenia
Bush Hammered Cenia
Honed Cenia
Sandblasted Cenia
ASTM TEST (U.S. Standars )
Absorption and bulk specific gravity. ASTM C-97
Absorption: 1,06 %
Bulk specific gravity: 2635Kg/m3
Compressive strength. ASTM C-170
Compressive strength in dry conditions (Mpa): 187 ± 39,3
Compressive strength in saturated conditions (Mpa): 160 ± 17,1
Flexural strength. ASTM C-880
Flexural strength in dry conditions (Mpa): 11,5 ± 1,7
Flexural strength in saturated conditions (Mpa): 10,6 ± 2,5
Modulus of rupture. ASTM C-99/ C-99 M-09
Average value of modulus of rupture in dry condition (Mpa): 12,6 ± 3,4
Average value of modulus of rupture in wet condition (Mpa): 12,9 ± 2,5
Abrasion resistance. ASTM C 1353-09
Average value of abrasion resistance index: 32,1
7.8 Mpa
12,6 Mpa
Abrassion resistance ( maximum value)
23,5mm
Open porosity:
3,7 %
Density: 4449,6 Lb/yd³
2620 Kg/m3
Water absortion at atmospheric pressure
(average value)
1%
Flexing resistance (average value)
16,3 Mpa
Abrassion resistance (average value)
22,5 mm
Resistance to compression (average value)
201 Mpa
Resistance to compression (minimum value)
157 Mpa
Resistance to sliding in wet conditions ¨Sawn
finish” (minimum value)
33
Resistance to sliding in wet conditions ¨Sawn
finish” (average value)
37
Resistance to sliding in wet conditions
in “flamed finish” (minimum value)
69
Resistance to sliding in wet conditions
in “flamed finish” (average value)
71
Frost resistance: 252 Cycles
TESTED IN THE NATURAL STONE LABORATORY OF THE
“CENTRO TECNOLOGICO DEL MARMOL” IN MURCIA (SPAIN)
CENIA STONE
3
Zoco Beirut Shopping Center (Lebanon)
Finish: Polished Cenia
Sheraton Maui Resort, Hawai (USA)
Finish: Flamed Cenia
4
CENIA STONE
CENIA STONE
5
American Embassy
(Germany)
Finish: Honed Cenia
Midsummer Place Shopping Center,
Milton Keynes (U.K.)
Finish: Honed Cenia
Helen and Martin Kimmel Building, New York University (USA)
Arq./Arch. Kevin Roche Jhon Dinkeloo Associates
Swiss Bank Corporation, Basel (Switzerland)
Finish: Sandblasted Cenia
Finish: Flamed Cenia
6
CENIA STONE
CENIA STONE
7
Perpignan (France)
Finish: Flamed Cenia
Fleury d’aude (France)
Promenade des Barques cours Mirabeau, Narbonne (France)
Finish: Flamed Cenia
8
CENIA STONE
Finish: Flamed Cenia
CENIA STONE
9
(Under construction. April, 2014)
Supreme Education Council Headquarter, Doha (Qatar)
Finish: Flamed Cenia / Honed Cenia
10
CENIA STONE
CENIA STONE
11
Prado Museum, Madrid (Spain)
Arq./Arch Rafael Moneo y Rafael Olalquiaga
Finish: Polished Cenia
Villanueva building, Madrid
Prado National Museum was constructed during
Carlos the IIIrd’s kingdom in 1785. It was directly
ordered by the king and his cabinet of intellectuals
to architect Juan de Villanueva. During its current
renewing and maintenance process, Ulldecona’s
Stone has been used to pave new museum areas.
Ahmed Bey Square,
Constantine (Algeria)
Spanish Olympic Headquarter, Madrid (Spain)
Finish: Flamed
Finish: Sandblasted Cenia
12
CENIA STONE
CENIA STONE
13
La Moraleja
Shopping Center, Madrid (Spain)
F.C. Barcelona Stadium,
Barcelona (Spain)
Finish: Flamed Cenia
Finish: Polished Cenia
Cortefiel Stores, around the world
L’Illa Diagonal Shopping Center, Barcelona (Spain)
Arq./Arch. Rafael Moneo y Manuel de Solá-Morales
Finish: Polished Cenia
Terminal T-2 . Barcelona airport. (Spain)
Finish: Polished Cenia
14
CENIA STONE
CENIA STONE
15
Edition: April 2015
The Cenia Stone Company
www.ceniastone.com
CENIA STONE
[email protected]
[email protected]
Tel. + 34 977 72 04 03
Fax + 34 977 72 13 07
INDUSTRIAL MARMOL EXPORT S.A.
Polígono Industrial “Planas Altas” s/n
Ctra. Vinaròs-Ulldecona, Km 10,9
P.O. Box 427
12500 Vinaròs (Castellón) SPAIN