Technical Information
PROCESSING INSTRUCTION
senotherm® - UHT 600
®
senotherm UHT 600
1.
STORAGE AND PREPARATION OF COATING PROCESS
1.1
QUALITY CONTROL OF MATERIALS ON RECEIPT
Product
No.:
Productseries/Article
series/Article No.:
-11551155
New supplies should be controlled with respect to the following parameter:
a)
Actual quantity supplied should correspond to the quantity indicated on the delivery note.
b)
Packaging supplied should be checked visually, so as to ensure that they were not damaged
during transport.
c)
Supply viscosity should be conform to the values indicated in the according technical data
sheet.
1.2
STORAGE
Material should preferably be stored at temperatures between 15° C and 25° C (59°F and 77 °F).
The warehouse should meet official regulations regarding storage. Storage should further be
organised according to the principle first in -first out, so that older batches are processed first.
When planning coating jobs, it should be taken into consideration that colour and degree of gloss of
different batches may vary slightly. For this reason coating of diverse parts of one product should - if
possible - only be coated with lacquer out of one batch.
If shelf life of the coating to be processed has already expired (we grant 6 months from
manufacturing date), it should be verified in time whether lacquer is still in good condition and allows
further processing. Respective criteria are: viscosity, a smooth and homogeneous surface as well as
colour of a trial coating. It should be ensured that material is homogenised thoroughly!
1.3
PREPARATIONS FOR COATING PROCESS
Prior to processing material must be brought to room temperature and stirred thoroughly High-speed
stirrers are to be preferred. Slowly running stirrers - integrated in many pressure tanks - are not
suitable for homogenisation, in particular in case of sedimentation. It is to be ensured that no
humidity comes into the material, as this negatively influences shelf life. Until next use, drums
should be closed again tightly.
In general, an adjustment of viscosity is not necessary, as material is supplied at application
viscosity. The system used for application of the coating should be equipped with a pre-filter with
large mesh size (> 500 µm/ < 35 mesh).
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Should coating material out of drums that had already been opened be used, please note that any
skin that may have formed can not be stirred into the material again, but has to be removed.
WEILBURGER Coatings GmbH
Ahaeuser
Weg 12-22
| D-35781GmbH
Weilburg/Lahn (Germany)
WEILBURGER
Coatings
Tel.:
+49 6471
315-0
| Fax:
+49 6471Weilburg/Lahn
315-116
Ahaeuser
Weg
12-22
| D-35781
(Germany)
E-Mail:
[email protected]
Tel.: +49
6471 315-0 | Fax: +49 6471 315-116
Internet:
www.weilburger-coatings.com
E-Mail: [email protected]
Internet: www.weilburger-coatings.de
Amtsgericht Limburg a.d. Lahn
HRB
3397 | Ust.-ID-Nr.
112637840
Amtsgericht
LimburgDE
a.d.
Lahn
Managing
Director:
Frank Gläser
HRB 3397
| Ust.-ID-Nr.
DE 112637840
Geschäftsführer:
page
1 of
9
Frank
Gläser,
Antonio Cuddemi
page 1 of 9
senotherm® - UHT
600
®
senotherm UHT 600
Product series/Article No.:
1155
-1155-
2.
COATING LINES
senotherm® coatings of series -1155- can be successfully applied by means of a variety of
application methods.
In general, however, this coating is applied via spray lines with conventional high-pressure air
atomization or via HVLP-systems. Other application systems are – after specific testing and
verification – possible. For the sealing of sockets and pipe couplings Teflon tape in combination with
Loctite glue has proven of value in practice. Mere hamp packs or self-cutting threads are not suited.
Depending on the geometry of the items or desired throughput /passage, it is also possible to apply
material via customary air-assist electrostatic systems. However, as the products are not adjusted for
ESTA spray, it would be reasonable to inform us on this particular requirement prior to placing the
order, so as to avoid any processing problems.
An application by means of brush and flow coating is - because of the poor surface quality that would
be achieved - generally not suitable. Due to the materials limited stability with regard to incorporation
of humidity, an application by means of dip coating is impossible.
Standard types are also available in spray cans.
All parts carrying the lacquer, as e.g. pipes, seals etc. must offer sufficient resistance against
hydrocarbons as e.g. xylene and benzine.
Prior to application of another system, the line should be cleaned with thinner 00-9597-100.066 or
another suitable quality.
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
3.
SUBSTRATES
This coating material allows use of the following substrates: aluminium, steel, stainless steel as well
as temperature-resistant combined materials e.g. aluminised steel, chromized steel and Galvalumes.
As is the case with most coating processes, the kind and quality of pretreatment has a considerable
influence on the quality of the final finish and hence its durability. The enclosed list indicates possible
combinations of substrates and pretreatments. In general, abrasive pretreatments lead to better
mechanical properties, however, minimum necessity is at any rate a clean, metallically pure
substrate that is further free from grease. For colours such as white, blue, red etc. a sanding is
imperative. Corrosion products (layers of rust or mill scale etc.) must be completely removed prior to
application.
As the requirements, depending on the end use, vary considerably, each new material and
processing combination should be tested with respect to its suitability for the respective application
prior to use. As a rule, substrates should - after pretreatment - be coated as soon as possible in
order to avoid belated contamination, the formation of oxide layers and the addition of humidity. If an
intermediate storage is necessary, items should be stored in tempered rooms with only insignificant
temperature changes, to avoid the formation of water of condensation.
WEILBURGER
Coatings
GmbH
WEILBURGER
Coatings
GmbH
AhaeuserWeg
Weg
12-22
| D-35781
Weilburg/Lahn
(Germany)
Ahaeuser
12-22
| D-35781
Weilburg/Lahn
(Germany)
Tel.:+49
+496471
6471315-0
315-0
| Fax:
315-116
Tel.:
| Fax:
+49+49
64716471
315-116
E-Mail:[email protected]
[email protected]
E-Mail:
Internet:www.weilburger-coatings.com
www.weilburger-coatings.de
Internet:
AmtsgerichtLimburg
Limburg
Lahn
Amtsgericht
a.d.a.d.
Lahn
HRB3397
3397
| Ust.-ID-Nr.
DE 112637840
HRB
| Ust.-ID-Nr.
DE 112637840
Geschäftsführer:
Managing
Director: Frank Gläser
Frank Gläser, Antonio Cuddemi
page
page2 2ofof9 9
senotherm® UHT
600
PROCESSING
INSTRUCTION
4.
-1155-
1155
PROCESSING
If possible, application should be made under constant conditions as e.g. temperature and
atmospheric humidity. As this is hardly fully feasible in practice, processing parameter as for instance
supply and atomizing pressure must be adjusted under consideration of the changed conditions.
PROCESSING SHOULD PREFERABLY BE MADE OUT OF CLOSED SYSTEMS AS E.G. PRESSURE TANKS, IN
ORDER TO REDUCE THE INCORPORATION OF HUMIDITY AS MUCH AS POSSIBLE. THIS INCORPORATION OF
HUMIDITY NEGATIVELY INFLUENCES STORAGE STABILITY. IF HAND GUNS ARE USED, DRUMS MUST BE CLOSED
AGAIN TIGHTLY AFTER EACH TAKING OUT OF LACQUER. SPRAY GUNS SHOULD ALSO BE CLOSED DURING
APPLICATION. TUBES AND PIPES MUST BE CLEANED AND RINSED AT THE END OF THE WORKING SHIFT AND
PRIOR TO LONGER INTERRUPTIONS/ BREAKS OF WORK.
For conventional high-pressure atomisation nozzle sizes of 1 - 2 mm with atomizing pressures of 2 5 bar (30-70 Psi) can be used. In practice nozzle sizes of 1,3 - 1,5 mm and atomizing pressures of
2,5 - 4 bar (36 – 58 PSI) have proven to be advantageous.
AS A RULE, IT IS TO BE TAKEN CARE THAT MAXIMUM FILM THICKNESS IS NOT EXCEEDED, AS THIS DOES NOT
ONLY INCREASE MATERIAL COST, BUT MAY ALSO LEAD TO QUALITY PROBLEMS AS FOR INSTANCE CRACKING,
PEELING OR ROLLING OFF IF EXPOSED TO RAPIDLY CHANGING TEMPERATURES.
5.
CURE
senotherm® paints of series -1155- are airdrying.
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Under standard conditions (20° C (68 °F) and 50 % relative atmospheric humidity) and if applied at
film thickness of 25 microns( 1 mil), films are dust dry after approx. 20-30 minutes and dry to touch
after approx. 1-2 hrs.
During airdrying methylalcohol is released. Therefore it is necessary to take care for proper
ventilation!
In practice, however, these values may – especially depending on the ambient temperature, the
atmospheric humidity and the dry film thickness – vary.
At temperatures below 10° C (50 °F) there is no sufficient through drying
Full properties are achieved after airdrying of 7 days. If items are subjected to temperature prior to
complete drying (at least 2 days), subject system may also release visible fumes when being put into
operation for the first time.
Ahaeuser Weg 12-22 | D-35781 Weilburg/Lahn (Germany)
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
E-Mail:
[email protected]
WEILBURGER
Coatings GmbH
Internet:
Ahaeuser
Weg 12-22 | D-35781 Weilburg/Lahn (Germany)
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
HRB 3397 | Ust.-ID-Nr. DE 112637840
Managing Director: Frank Gläser
page
of 9 | Ust.-ID-Nr. DE 112637840
HRB33397
Geschäftsführer:
senotherm® - UHT
600
®
senotherm UHT 600
1155
-1155-
6.
QUALITY AND APTITUDE TESTS
Due to the broad field of application, a great number of test methods for quality and aptitude tests exists. The
below table provides a survey on customary tests, however, does not claim to be complete.
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Test
Non-volatile substances
Determination of efflux time
(viscosity)
Measuring of film thickness
Cross-hatch test
Water of condensation
Constant climate
Temperature charge
Salt spray test
Standard
DIN EN ISO 3251
DIN 53 211
Differing Conditions
4 mm cup at 23°C
DIN 50 981; DIN 50 982
ISO 2409
DIN 50 017 KK
ST 029
DIN 50 021 SS
WEILBURGER
Coatings
GmbH
WEILBURGER
Coatings
GmbH
AhaeuserWeg
Weg
12-22
| D-35781
Weilburg/Lahn
(Germany)
Ahaeuser
12-22
| D-35781
Weilburg/Lahn
(Germany)
Tel.:+49
+496471
6471315-0
315-0
| Fax:
315-116
Tel.:
| Fax:
+49+49
64716471
315-116
[email protected]
E-Mail:
Internet:
AmtsgerichtLimburg
Limburg
Lahn
Amtsgericht
a.d.a.d.
Lahn
HRB3397
3397
| Ust.-ID-Nr.
DE 112637840
HRB
| Ust.-ID-Nr.
DE 112637840
Geschäftsführer:
Managing
page
page44ofof9 9
Technical
Information
®
senotherm UHT 600
Productseries/Article
series/Article No.:
Product
No.:
1155
-1155-
7.
SUBSTRATES
Substrate
Sheet metal
Cast iron
Aluminised steel
Hot dip, Sendzimir
and electrolytically
galvanized steel
Galvan (hot-dip galva-
nized steel, however Zn,
95 % + 5 % Al)
Galvalum(hot-dip gal-,
vanized steel, however
45 % Zn+ 55 % Al)
Rolled aluminium
e.g. Al 99,5
Cast aluminium
Stainless steel
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Non-glazed ceramics
Fire clay
Pretreatment
degrease
degrease &
phosphatization
degrease &
sandblasting
degrease &
sandblasting
degrease &
phosphatization
degrease
degrease &
chromatization
degrease
degrease
degrease &
chromatization
degrease
Degrease &
chromatization
degrease
degrease &
chromatization
degrease & caustic
wash
degrease &
sandblasting
(corundum)
degrease &
polishing
degrease &
sandblasting
(corundum)
degrease
degrease &
chromatization
degrease &
sandblasting
(corundum)
degrease
Suitability
limited suitability
limited suitability
suitable
suitable
Remarks
At temperatures exceeding approx. 200 ° C
an oxide layer forms that can lead to a loss of
coating’s adhesion.
Low carbon (that can be enamelled) steels
show considerably better results.
limited suitability
see sheet metal
limited suitability
Suitable up to approx. 500° C. Temperatures
exceeding 500° C lead to an aludipping.
The change of volume entailed with this
phenomenon may cause adhesion problems.
limited suitability
limited suitability
limited suitability
limited suitability
Due to the restructuring of the zinc layer
at temperatures exceeding 200° C
peeling off may be caused. If exposed to
vapours, there is the danger of loss of
adhesion.
limited suitability
suitable
suitable
suitable
well suited
suitable
well suited
Structural changes of the aluminium from
temperatures exceeding 200° C. This leads
to changes in stability.
Corrosion resistance and adhesion
considerably depend on the
alloy used.
See rolled aluminium. A high silicon content
(from approx. 11 %)
can lead to non-homogeneous alloys and
hence to different properties on the item
limited suitability
limited suitability
well suited
limited suitability
Visual appearance heavily depends on
absorbency.
AS A RULE, EVERY MATERIAL COMBINATION HAS - PRIOR TO APPLICATION - BE TESTED WITH RESPECT TO ITS SUITABILITY.
WEILBURGER
Coatings
Ahaeuser
Weg 12-22
| D-35781GmbH
Weilburg/Lahn (Germany)
Ahaeuser
Weg
12-22
| D-35781
(Germany)
Tel.:
+49 6471
315-0
| Fax:
+49 6471Weilburg/Lahn
315-116
Tel.: +49
6471 315-0 | Fax: +49 6471 315-116
E-Mail:
[email protected]
Internet:
Amtsgericht
LimburgDE
a.d.
Lahn
HRB
3397 | Ust.-ID-Nr.
112637840
HRB 3397
| Ust.-ID-Nr.
DE 112637840
Managing
Director:
Frank Gläser
Geschäftsführer:
Frank
Gläser,
Antonio Cuddemi
page
5 of
9
page 5 of 9
®
senotherm UHT 600
-1155-
1155
QW-4.2-Nr.528e-1-08/08
4.2-Nr.528e-1-08/08
The above indications were determined under lab conditions and in practice as being reference values. They correspond to today’s
developments in technique. Application equipment and application technique are beyond our influence. This information is given to the
best of our knowledge, however, no liability or obligation whatsoever is assumed in connection with it.
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
Internet: www.weilburger-coatings.com
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
HRB 3397 | Ust.-ID-Nr. DE 112637840
page 6 of 9
HRB 3397 | Ust.-ID-Nr. DE 112637840
Geschäftsführer:
Technical
Information
senotherm - UHT
600
®
®
senotherm UHT 600
1155
-1155-
Drying process at different temperatures and atmospheric humidities after a flash off of 15 min. at room temperature
Degrees of drying:
1.) Surface is still wet
2.) Surface is dry; Coating can be easily wiped off with the finger so that the
substrate is exposed.
3.) Coating can no longer be wiped off, however, traces of the wiping can be
seen.
4.) No traces of the wiping can be seen; The surface can be harmed with the
finger.
5.) It is difficult to penetrate into/scratch the coating film with the fingernail.
6.) The coating film is dried through and can no longer be harmed with the
fingernail.
Drying process 1155
30% atmospheric humidity
7
Degree of drying
6
10°C
5
20°C
30°C
4
40°C
3
50°C
60°C
2
70°C
1
0
15
30
45
60
75
90
105
120
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Drying time
Tel.:
| Fax:
+49+49
64716471
315-116
Tel.:+49
+496471
6471315-0
315-0
| Fax:
315-116
E-Mail:
[email protected]
Internet:
HRB 3397 | Ust.-ID-Nr. DE 112637840
HRB 3397 | Ust.-ID-Nr. DE 112637840
Managing
Geschäftsführer:
page 7 of 9
page 7 of 9
senotherm® - UHT
600
PROCESSING
®
INSTRUCTION
senotherm UHT 600
-1155-
1155
Drying process 1155
50% atmoshperic humidity
7
Degree of drying
6
10°C
5
20°C
30°C
4
40°C
3
50°C
60°C
2
70°C
1
0
15
30
45
60
75
90
105
120
QW-4.2-Nr.528e-1-08/08
QW-4.2-Nr.528e-1-08/08
Drying time
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
Internet: www.weilburger-coatings.com
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
HRB 3397 | Ust.-ID-Nr. DE 112637840
HRB 3397 | Ust.-ID-Nr. DE 112637840
page 8 of 9
Geschäftsführer:
page 8 of 9
PROCESSING
INSTRUCTION
senotherm® UHT
600
-1155-
1155
Drying process 1155
70% atmoshperic humidity
7
Trocknungsstufe
6
10°C
5
20°C
30°C
4
40°C
3
50°C
60°C
2
70°C
1
0
15
30
45
60
75
90
105
120
Drying time
ALL VALUES HAVE BEEN DETERMINED UNDER LAB CONDITIONS AND MAY – DEPENDING ON THE GEOMETRY OF THE
ITEMS, THE APPLICATION METHOD AND THE FILM THICKNESS – VARY IN PRACTICE.
QW-4.2-Nr.528e-1-08/08
W-4.2-Nr.528e-1-08/08
M:\Datenblaetter\infoengl\1155ProcessingInstructions-08.doc
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
WEILBURGER
Coatings GmbH
Internet:
Tel.: +49 6471 315-0 | Fax: +49 6471 315-116
22.02.2010/hh
HRB 3397 | Ust.-ID-Nr. DE 112637840
Amtsgericht
page
9 of 9 Limburg a.d. Lahn
HRB 3397 | Ust.-ID-Nr. DE 112637840
Geschäftsführer:

PDF - Weilburger Coatings GmbH

Transcription

Similar documents

Dear Members and Friends - Trinity Lutheran Church Of Indio

credit card payment sample page for visa/mastercard

Program Booklet - The Chesapeake Bay String of Pearls Project

Greetings from The Squirettes of Mary Immaculate, Youth Arm of the

TEST OR INSPECTION ITEM FREQUENCY REQUIREMENTS

Change of board hiking tour

Refrigerated Compressed Air Dryers

Pope John Paul II`s Teaching on Sexuality and Marriage: An Appraisal

Wattyl Hammer Finish is high quality fast drying enamel featuring an