Okapox GF-M page 1 of 3
Multipurpose Epoxy Resin
Okapox GF-M
 solvent and water free
 very low emission
 high bond strength for repairing cracks in screed and
concrete
 suitable as primer or moisture barrier
 suitable as vapor barrier
 suitable as binder for epoxy mortars
 suitable to fill and seal any penetration in a stem room environment
Product Description
Multipurpose two-component epoxy resin with high bond strength suitable for repairing cracks in screed and
concrete and as primer for absorbent and non-absorbent substrates before leveling and installation work.
Okapox GF-M is also suitable as barrier against moisture in cement-based substrates and as binder for epoxy
mortars
Substrate preparation
The substrate must be clean and load-bearing. Remove all dry and unsound debris/imperfections
mechanically. In high stress areas the substrate has to be suitable to withstand the expected load.
Processing
Puncture bottom of part B container several times with a screwdriver. Let the entire hardening fluid flow into
the lower container. Remove empty container and mix the two components thoroughly with an electric mixer
until the mixture is without streaks.Repot and stir again.
For repairing cracks:
The parts to be glued must be dry, clean and solid. Enlarge screed cracks so that the resin can penetrate into
2/3 of the screed layer. In addition cut into 2/3 of the screed layer perpendicular to the crack every 3“ to 1 ft.
(10 -30 cm) with a grinder, vacuum, set a steel spike or screed repair clamp, fill with Okapox GF-M resin and
scatter quartz sand on fresh surface immediately.
As primer:
Apply Okapox GF-M evenly onto surface with a lamb skin roller. Scatter a fair amount of quartz sand (0.6 - 1.2
mm grain) onto the fresh surface (coverage approx. 2.5kg/m²).
As moisture barrier:
Apply at least 400 - 500 g/m² of Okapox GF-M to create a moisture barrier to block residue moisture of 7,0
weight% in concrete floors and 5,0 weight% in cementscreeds.
As epoxy mortar:
Mix Okapox GF-M to a homogenous consistency and add up to 3 kg quartz sand (0.6- 1.2 mm grain). To fill
holes prime the edges first with pure Okapox GF-M and fill wet in wet with mortar.
Kiesel Bauchemie GmbH u. Co. KG
Wolf-Hirth-Straße 2
D-73730 Esslingen
Telefon: 0711 93134-0
Telefax: 0711 93134-140
www.kiesel.com
Niederlassung:
D-39590 Tangermünde
Telefon: 03 93 22 95-0
Geschäftsführung:
Wolfgang Kiesel
Dr. Matthias Hirsch
Persönlich haft. Gesellschafterin:
Kiesel Verwaltungsges. mbH
Amtsgericht Stuttgart HRB 210484
Sitz der Gesellschaft:
73730 Esslingen
Amtsgericht Stuttgart HRA 210806
Technical Data Sheet
Okapox GF-M page 2 of 3
Specifications
Color
yellowish transparent
Application
interior and exterior, walls and floors
Density
1,20 g/cm³
compressive strength
approx. 60 N/mm² /approx. 40 N/mm² with quartz
sand
flexural strength
approx. 35 N/mm²/approx. 16 N/mm² with quartz
sand
adhesive strength
stronger than concrete
Application temperature
50°F to 86°F (+10°C to +25°C ) (substrate)
Temperature tolerance
-20°C to +60°C (-4°F to 140°F)
mixing ratio
750 g can: 600 g Comp.. A / 150 g Comp.. B
processing time*
approx. 10 min. / approx. 30 min. with puartz sand.
Curing period *
after approx. 7 days
Floor heating system
suitable
Ready for traffic * / ready for installation *
approx. 90 - 120 min. as crack filler approx. 12
hours as moisture barrier an epoxy mortar
Marked according GefStoffV
Component A: irritant Component B: corrosive
GISCODE
RE 1 according to TRGS 610
EMICODE
EC-1 R according to GEV
storage
store in dry area for up to 12 months
*
At 68°F (+20°C) and 65% relative humidity. Higher
temperature and low humidity decreases, lower
temperature and high humidity increases this value
respectively.
Coverage
approx. 300 g/m² as primer
Cleaning
Clean tools with Okapox GF-V.
Kiesel Bauchemie GmbH u. Co. KG
Wolf-Hirth-Straße 2
D-73730 Esslingen
Telefon: 0711 93134-0
Telefax: 0711 93134-140
www.kiesel.com
Niederlassung:
D-39590 Tangermünde
Telefon: 03 93 22 95-0
Geschäftsführung:
Wolfgang Kiesel
Dr. Matthias Hirsch
Persönlich haft. Gesellschafterin:
Kiesel Verwaltungsges. mbH
Amtsgericht Stuttgart HRB 210484
Sitz der Gesellschaft:
73730 Esslingen
Amtsgericht Stuttgart HRA 210806
Technical Data Sheet
Okapox GF-M page 3 of 3
Packaging
Packaging
Item no.
750 g (1.7 lbs) two compartment tin can
48027
The aforementioned information, especially the proposals for processing and utilizing our product, is based
on our knowledge and experience. We recommend that you carry out your own tests in every case to ensure
the suitability of our products for the intended process and processing purposes because of the different
materials and the working conditions which lie beyond our area of influence. No liability can be derived from
this advice or from verbal advice, unless we are responsible for (criminal) intent or gross negligence in this
respect.
Revised: 25.08.08 au
Kiesel Bauchemie GmbH u. Co. KG
Wolf-Hirth-Straße 2
D-73730 Esslingen
Telefon: 0711 93134-0
Telefax: 0711 93134-140
www.kiesel.com
Niederlassung:
D-39590 Tangermünde
Telefon: 03 93 22 95-0
Geschäftsführung:
Wolfgang Kiesel
Dr. Matthias Hirsch
Persönlich haft. Gesellschafterin:
Kiesel Verwaltungsges. mbH
Amtsgericht Stuttgart HRB 210484
Sitz der Gesellschaft:
73730 Esslingen
Amtsgericht Stuttgart HRA 210806