Technical Brochure

Comments

Transcription

Technical Brochure
The durable, contemporary timber
solution.
Internal
Cover photo:
Guipuzcoan Football Federation
Project: Izaskun Larzábal
Photography: Susana Aréchaga and Luis M. Ambrós
Parklex 2000, Eucalyptus
Indoor wood
coverings.
The natural wood used to manufacture Parklex provides
a look of quality and comfort for building interiors from
the very first moment.
With Parklex, ceilings, walls and floors, in addition to
any other surface, such as counter tops, bathrooms
and even showers take on a new leading role.
If you’re looking for quality and comfort, Parklex has a
wide range of natural wood finishes that achieve both
purposes. In addition, its variety of finishes allows
decorators and architects to be creative with combinations
on any type of surface, allowing them to decorate the
floors, walls or ceiling in the same wood, providing the
degree of quality and comfort that only natural, highquality materials can convey.
Floor,
walls and
ceiling.
The same colors and
finishes throughout the
interior.
Parklex paneling may be installed on any surface:
floors, walls and ceilings, combining aesthetic elements
or keeping the same colors and finishes throughout
the interior, converting rooms into authentic enclosures,
completely lined with natural wood panels.
Recommended products:
· Floors:
2000
3000
· Walls and ceiling:
Dry areas:
500
Damp areas:
700
Quality at
your feet.
Recommended products:
· Floors:
2000
3000
The quality of Parklex comes from the materials and
processes used to manufacture them. This quality is
demonstrated precisely where the product suffers the
most wear: floors, transit spaces and areas of intensive
use, where any material suffers a high level of wear.
Parklex, however, performs at top levels in these areas,
with its properties remaining unchanged. Simple
maintenance is all that is needed to prolong the life of
these coverings, which makes them immediately
economical.
It demonstrates its
quality where it suffers
the most wear.
Silence:
another form
of comfort.
Recommended products:
· Walls and ceiling:
500
Noise and reverberation prevention is also a form of
comfort. Parklex 500 is designed to be installed as an
indoor wall and ceiling covering in locations with high
acoustic absorption requirements: conference halls,
presentation rooms, auditoriums, offices, etc., as well
as furniture coverings.
These panels insulate rooms from outside noise or that
of nearby areas, providing an even greater feeling of
comfort.
Coverings for locations
with high acoustic absorption requirements.
Excellent fire
behavior. Parklex
means peace of
mind.
Recommended products:
· Floors:
2000
· Walls and ceiling:
Dry areas:
500
Damp areas:
700
In addition to being manufactured from natural wood,
the entire Parklex line is tested according to the new
European standard EN 13.501 regarding reaction to
fire, obtaining the best results possible for organic
materials.
With Parklex, you are sure to make the right decision.
Natural wood with the
best results for reaction
to fire.
Bathrooms,
gymnasiums, spas
or pools: don’t
relinquish comfort.
Cozy, moisture resistant
spaces.
Moisture is a factor that generally determines the materials
used in bathrooms. Thanks to the production and treatment
processes Parklex uses on natural wood, it is now possible
to use Parklex coverings in any area of the bathroom,
even in the shower, transforming them into areas that are
just as inviting as the rest of the interior.
The Parklex line stands out for its moisture resistance,
which also allows its problem-free use in gymnasiums,
spas or pools, making these areas (and any other space
where appearance, hygiene, resistance and cleanliness
are important) exclusive places that are both pleasant and
totally unique.
Recommended products:
· Walls and ceiling:
Damp areas:
700
· Floors (bathrooms and
gymnasiums):
2000
Parklex
Projects
Guggenheim
Bilbao
Bilbao, Spain.
Architect: Frank O. Gehry
Project manager: César Caicoya
Parklex 2000, Museum Ash
Bilbao, May 14, 2007
Bilbao, 14 de mayo de 2007
Dear Sirs:
Estimados Señores:
After ten years of intensive use, withstanding the regular heavy machinery
traffic and the exposition of sculptures
weighing many tons, we would like to
express our satisfaction with the wood
floors in the Guggenheim Museum galleries (Manufacturer: Composites Gurea, model Parklex 2000, lightened
ash), with regards to both the ease of
cleaning
and their durability and strength.
Rogelio Diez
Maintenance and Installations Supervisor
Tras diez años de funcionamiento intensivo de los suelos
de madera en las Galerías del Museo Guggenheim
(Fabricante Composites Gurea, modelo Parklex 2000,
fresno clarificado), soportando el paso habitual de
maquinaria pesada y la exposición de esculturas de gran
tonelaje, comunicamos nuestra satisfacción con los
mismos, tanto en su facilidad de limpieza como en su
durabilidad y resistencia.
Navarran
Government
Press Room
Pamplona, Spain.
Architects: Javier Barcos Berruezo
and Manolo Enríquez Jiménez
Parklex 500, Walnut
Parklex 2000, Walnut
Marqués de Riscal
Hotel
The Luxury Collection.
Alava, Spain.
Architect: Frank O. Gehry
Project manager: César Caicoya
Parklex 500, Maple
Parklex 2000, Maple
Cepa 21 Wineries
Valladolid, Spain.
Architects: BSA Arquitectos
Interior design: TGA+Asociados
and Javier Machimbarrena
Parklex 500, Maple
Burlada Cultural
Center
Navarre, Spain.
Architect: Miguel Ayate Bariain
Parklex 500
Puerta de America
Hotel
Madrid, Spain.
Architect: Jean Nouvel
Parklex 2000
Zubieta XXI Sports
Complex
Guipuzcoa, Spain.
Project: Izaskun Larzábal, Fernando
Gárate and Agustín Oteiza
Photography: Susana Aréchaga
and Luis M. Ambrós
Parklex 2000, Natural Beech
De la Peña Station
Bilbao, Spain.
Architect: GPD Studio
Parklex 500
La Perla Hotel
Pamplona, Spain.
Architect: Javier Martínez Oroquieta
Parklex 500, Walnut
Parklex 2000, Walnut
Thermae Bath Spa
The Minerva Bath.
Bath, United Kingdom.
Architect: Nicholas Grimshaw & Partners
Photography: Matt Cardy
Parklex 700, Maple
Guipuzcoan
Football
Federation
Guipuzcoa, Spain.
Project: Izaskun Larzábal
Photography: Susana Aréchaga
and Luis M. Ambrós
Parklex 2000, Eucalyptus
Attic in San
Sebastian
Guipuzcoa, Spain.
Interior design: Verónica Conejos
Parklex 2000, Museum Ash
COEC, Catalonian
Odontologist and
Stomatologist
Association
Barcelona, Spain.
Architect: Pere Fosch i Alvarez
Parklex 3000, Maple
Beroa Bar
Guipuzcoa, Spain.
Design: Formak Studio
Parklex 2000 (floor)
Parklex 3000, Zebrano (bar)
Home in
Pamplona
Navarre, Spain.
Interior design: Héctor Elizaga
Photography: Susana Aréchaga
and Luis M. Ambrós
Parklex 2000, Maple
Air France, VIP
Lounge
Narita International Airport.
Tokyo, Japan.
Architect: Noé Duchaufour-Lawrance
Parklex 500, Reconstituted Oak
Parklex 2000, Reconstituted Oak
Electronics Arts
London, United Kingdom.
Architect: Foster + Partners
Photography: Nigel Young
Parklex 2000, Natural Beech
Amrey Hotel
Barcelona, Spain.
Architect: Ramón Domenech
Parklex 2000, Maple
Home in San
Sebastian
Guipuzcoa, Spain.
Interior design: Javier Machimbarrena
Photography: Susana Aréchaga
and Luis M. Ambrós
Parklex 2000, Walnut
Home in Puerto
Pollença
Majorca, Spain.
Architect: Joan Riusech
Photography: Susana Aréchaga
and Luis M. Ambrós
Parklex 2000, Maple
Technical
characteristics
About Parklex
Production process
Each type of Parklex is subjected to a different production
process, depending on its final application: interiors, exteriors,
damp areas, etc.
The base is always high-density laminated wood with a paper
fiber core that has been treated with thermosetting resins and
compressed at high pressure and temperature.
Finishes
Perfect adaptation to the project design is an essential requirement. That’s why the technology used to manufacture Parklex
allows us to apply different finishes, all in natural wood, to
integrate them completely into the environment that is required
for each project.
International
Providing service on an international level has meant establishing an extensive network of Parklex distributors on all five
continents. This allows us to work more closely with our clients
and offer them better service in a way that is more accessible
to them. It also lets us understand their needs perfectly and
first hand.
Guarantees / Quality Certificates
Rigorous testing guarantees Parklex’s excellent performance.
Natural wood
The surface is always made from 100% natural wood, treated
according to its application: to resist special weather conditions
or to perfectly resist the intensive use it might receive in
interiors.
Range
The variety of finishes and colors in natural and dyed panels
sets Parklex apart as a result of its versatility, making it the
ideal covering from any type of project.
Architects
The best architects in the world use Parklex in their most
emblematic creations. Why is this so? Because they feel
comfortable and at ease, and because the results do not
disappoint them. Without a doubt, it is because at Parklex we
have been working for over 15 years on a daily basis with
architects from all over the world, including, for example,
Santiago Calatrava, Frank Gehry, Norman Foster, Jean Nouvel
and Nicholas Grimshaw, adapting our range to their requirements. This has made Parklex the natural wood covering of
choice in many of the best quality and best-known projects in
the world.
This can only be achieved by a brand with an absolute
guarantee, capable of offering the perfect product, totally
adapted to their needs, with problem-free application.
Parklex – The ideal solution
Quality and performance are only the most visible results
of Parklex. As if this weren’t enough, the advantages
offered by Parklex are evident from the moment
it is installed, up to its long-term maintenance.
Characteristics
Ease of installation.
Maintenance.
The floating flooring system is simple and low-cost. The rest
of the products may be easily installed, following clear, professional instructions.
Parklex does not require any sort of scraping or varnishing
as part of its maintenance. It need only be lightly cleansed
with a mop, using liquid ph-neutral soap and water.
Acoustic absorption.
Service.
Parklex 500 and Parklex 700 may be perforated, making them
the ideal materials for acoustic absorption. They have been
manufactured specifically for interiors where the acoustic
factor is important.
Parklex has a technical support department to answer any
questions regarding product assembly and to give advice on
the most appropriate type of covering to meet every need.
Strength.
Quality.
Material for intensive use indoor areas is made with the highest
quality natural wood panels that have been impregnated using
the Gureprex system, which provides a series of benefits with
regards to abrasion, moisture resistance, hardness, scratch
resistance and dimensional stability that are far superior to
any of the varnish-treated products currently found on the
market.
Parklex means quality. All our products have earned the CE
mark and carry an absolute guarantee. Exterior panels are
manufactured according to the European standard EN 438,
which applies to HPL (high pressure laminates). This is why
Parklex is the covering preferred by the world’s most prestigious
architects.
Moisture resistance.
Fire behavior.
The technology used by Parklex to manufacture the exterior
coverings completely guarantees them against extreme weather
conditions: rain, sun, humidity and heat. This same technology
allows us to provide a material for interiors with identical
resistance properties. Parklex therefore provides the ideal
product for damp areas.
The entire Parklex line is classified according to the new
European standard EN 13.501-1:2002 regarding reaction to
fire, obtaining the best results possible for organic materials.
Parklex product guide
Damp areas
700
Stratified timber panels for internal use, with high resistance
to humidity.
Walls and
ceilings
Dry areas
500
Natural timber ceiling and wall
finishes.
Internal
Floating
parquet
2000
Natural timber floor for extreme wear environments.
Floors
Raised
flooring
3000
Natural timber finish for full
access raised floors.
External
Façades
Facade
High-density stratified timber
panels for external use.
700
Stratified timber panels for internal use,
with high resistance to humidity.
Parklex 700 is a high-density stratified natural timber panel,
made from kraft paper that has been treated with thermoset
resins compressed under high pressures and temperatures,
finished with natural timber veneers.
Finish range
(1) Panels manufactured from joined timber
veneers. There may be as many as 12 veneer
pieces in each full panel (16 in the case of
stained finishes).
Ambar (2)
Antra (2)
Ayous Natural
Black
Cherry (1)
Copper (2)
Eucalyptus (1)
Museum Ash (1)
Gold (2)
Grey Beech (1)
Natural Beech (1)
Green Beech (1)
Maple (1)
Walnut (1)
Onix (2)
Quartz (2)
Natural Oak (1)
Reconstituted Oak (1)
Rubi (2)
Sapelli (1)
Silver (2)
Wengue (1)
Natural Zebrano (1)
Surface characteristics
(2) Available only in a Smooth surface finish.
Woodskin®. A finish that allows you to
feel the grain and subtlety of natural
timber.
Special finishes
Smooth. Traditional Parklex finish.
Reveals the simple, natural beauty of the
wood it is manufactured with.
Assembly systems *
Chequerplate Rubber
Exposed fastening. The Parklex panels
are fastened with stainless steel screws
or rivets to the treated wood or metal
substructure.
Hidden fastening, with special hanging
profiles. The Parklex panels are attached
to the aluminum substructure, using guide
profiles and hanging pins.
Hidden fastening, using adhesive. The
Parklex panels are fastened using adhesive to the treated wood or metal substructure.
Hidden fastening, with caps. The Parklex
panels are attached with screws hidden
by caps with a diameter of 10,75mm and
a section of 2mm, using the same material
and finish as the panel.
* For more information on installation, consult the Internal Parklex Assembly Catalogue
or our web page (www.parklex.com).
Smooth Rubber
Chequerplate (3)
Perforated
Panel construction
Moisture resistant overlay
Natural timber veneer
HPL core
Natural timber veneer
Balancing film
HPL core
Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations of
printed media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklex
recommends consulting our sales personnel to request actual samples.
Technical characteristics
Thickness ≥ 6mm
Tests
Stand
Property or attribute
Measurement unit
1. Inspection
Colour, pattern and surface finish
Result
Parklex 700 CGS
(Standard)
Parklex 700 CGF
(Fire Class)
Rev: 03 (09.2009)
Rev: 03 (09.2009)
EN 438-8 Part 5.2.2.3
Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structure differences
are considered as normal. Singularities such as knots and resin inclusions are not considered as defects, but as a part of the
décor. There are differences in light fastness performances depending on the wood species and the source of the wood.
EN 438-2 Part 5
6,0 ≤ t < 8,0
2. Dimensional tolerances
Thickness (t)
± 0,40
mm
8,0 ≤ t < 12,0
± 0,50
12,0 ≤ t < 16,0
± 0,60
16,0 ≤ t < 20,0
± 0,70
20,0 ≤ t < 25,0
± 0,80
Length and width
EN 438-2 Part 6
–
mm
+10 / - 0
Edge straightness
EN 438-2 Part 7
–
mm/m
1,5
Edge squareness
EN 438-2 Part 8
–
mm/m
1,5
EN 438.-2 Part 17
Cumulative dimensional change
(t≥6_mm)
% max Longrain
0,3
3. Physical properties
Dimensional stability at elevated temperatures
% max Crossgrain
Resistance to impact with large diameter ball
EN 438-2 Part 21
Maximum height for which no visible surface
cracking or imprint greater than 10mm
(t≥ 6mm)
Tensile strength
EN ISO 527-2
Longrain
0,6
mm
≥ 1.800
MPa
≥ 60
µ
110
N
> 2.000
Crossgrain
4. CE Safety requirements
Water vapour permeability
EN 438-7 Part 4.4
Wet cup method
Dry cup method
Resistance to fixings
EN 438-7 Part 4.5
Screw holding value t ≥ 6_mm
250
FScrew holding value t ≥ 8_mm
> 3.000
Screw holding value t ≥ 10_mm
> 4.000
Release of formaldehyde
EN 438-7 Part 4.11
Classification
Rating
E1
Flexural strength
EN ISO 178
Longrain
MPa
≥ 80
MPa
≥ 9.000
≥ 80
Crossgrain
Flexural Modulus
EN ISO 178
Resistance to inmersion in boiling water
EN 438-2 Part 12
Longrain
≥ 9.000
Crossgrain
Density
EN ISO 1.183
Moisture absorbed
%
≤2
Moisture absorbed
%
≤2
Appear
Degree
Density
g/cm3
Euroclass t ≥ 6_mm
Classification
Thickness* - Smooth finish
3, 6, 8, 10, 12,14, 18 & 22 mm
Thickness* - Chequerplate finish
10, 12,14, 18 & 22 mm
≤3
≤6
≥4
≥ 1,35
5. CE Safety requirements - Reaction to fire
Reaction to fire
EN 13.501-1
Panel dimensions
Length (grain direction) x width
2440 x 1220 mm
* 3 and 6 mm can only be used for special applications. Other thicknesses may be available upon request.
C-s2,d0
B-s2,d0
500
Natural timber ceiling and wall finishes.
Parklex 500 is a timber panel manufactured from 100% natural
timber fibres, pressed under high temperatures and impregnated with thermoset resins using our exclusive Gureprex
system.
Finish range
(1) Panels manufactured from joined timber
veneers. There may be as many as 12 veneer
pieces in each full panel (16 in the case of
stained finishes).
Ambar
Antra
Ayous Natural
Bamboo (1)
Black
Cherry (1)
Eucalyptus (1)
Museum Ash (1)
Grey Beech (1)
Natural Beech (1)
Green Beech (1)
Maple (1)
Walnut (1)
Onix
Natural Oak (1)
Reconstituted Oak (1)
Rubi
Sapelli (1)
Wengue (1)
Natural Zebrano (1)
Surface characteristics
Panel construction
Woodskin®. A finish that allows you to
feel the grain and subtlety of natural
timber.
Gureprex wear resistant overlay
Natural timber veneer
Resin bonded WBP plywood core
HPL balancer
Wood
Acoustics
Assembly systems *
Parklex 500 acoustic is designed for
interior wall and ceiling finishes requiring
high levels of acoustic absorption.
It is machined in different forms and
dimensions allowing for the desired level
of acoustic performance.
Slots
Perforated
Exposed fastening. The Parklex panels
are fastened with stainless steel screws
or rivets to the treated wood or metal
substructure.
Hidden fastening, with special hanging
profiles. The Parklex panels are attached
to the aluminum substructure, using guide
profiles and hanging pins.
Hidden fastening, using adhesive. The
Parklex panels are fastened using adhesive to the treated wood or metal substructure.
Hidden fastening, with caps. The Parklex
panels are attached with screws hidden
by caps with a diameter of 10,75mm and
a section of 2mm, using the same material
and finish as the panel.
* For more information on installation, consult the Internal Parklex Assembly Catalogue
or our web page (www.parklex.com).
Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations of
printed media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklex
recommends consulting our sales personnel to request actual samples.
Technical characteristics
Thickness ≥ 8mm
Tests
Standard
Property or attribute
Measurement unit
1. Inspection requirements
Colour, pattern and surface finish
EN 438-8 Part 5.2.2.3
Result
Parklex 500 VDS
(Standard)
Parklex 500 VDF
(Fire Class)
Rev: 03 (09.2009)
Rev: 03 (09.2009)
Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structure
differences are considered as normal. Singularities such as knots and resin inclusions are not considered as
defects, but as a part of the décor. There are differences in light fastness performances depending on the wood
species and the source of the wood
2. Dimensional tolerances
Thickness (t)
EN 438-2 Part 5
t = 6,0
mm
+1,0 / -0,6
t = 8,0
+1,6 / -1
+1,0 / -0,7
t = 11,0
+1,4 / -1,1
+1,2 / -0,8
t = 14,0
+1,6 / -1,1
+1,3 / -0,9
t = 17,0
+1,3 / -1,3
+1,4 / -1,0
t = 20,0
+1,3 / -1,1
+1,6 / -1,2
t = 40,0
+2,0 / -1,6
mm
≤0,6
–
mm
+10 / - 0
–
mm/m
1,5
EN 438-2 Part 8
–
mm/m
1,5
EN 438-2 Part 10
Resistance to surface wear
Initial wear point
≥ 50
Wear resistance
≥ 150
Tolerance for thickness variations inside a panel
EN 315:1993
Length and width
EN 438-2 Part 6
Edge straightness
EN 438-2 Part 7
Edge squareness
t (nominal thickness)
3. Physical properties
Revolutions
Resistance to surface wear
Resistance to inmersion in boiling water
EN 438-2 Part 12
Aspect
Rating
≥4
Resistance to scratching
EN 438-2 Part 25
Force
Rating
≥2
Lightfastness (xenon arc)
EN 438-2 Part27
Contrast
Grey scale rating
≥4
< 4 (A)
≥ 70
Longitudinal direction
Flexural strength
Flexural modulus
EN 310
MPa
Transversal direction
≥ 60
Longitudinal direction
≥ 7000
EN 310
MPa
≥ 6000
Transversal direction
Perpendicular tensile strength
ASTM C 297
Density
-
Adhesion force
MPa
Density
g/cm3
≥2
≥ 0,75
≥ 0,80
4. CE Safety requirements
Resistance to fixings
EN 438-7 Part 4.5
Force
N/mm
≥ 200
≥ 130
Bonding strength
EN 438-7 Part 4.7
Bond strength
MPa
≥ 1,42
≥ 2,64
Flexural tensile strength
EN 438-7 Part 4.8
Bond strength
MPa
≥ 1,42
≥ 2,64
Content of pentachlorophenol
EN 438-7 Part 4.10
Release of formaldehyde
EN 717-2
Glue-line quality
≤5
Content pentachlorophenol
ppm
Release of formaldehyde
Rating
EN 438-7 Part 4.13.3
Expression of results
Rating
Resistance to elevated temperature
EN 438-7 Part 4.13.3
Aspect
Result
Water resistance
EN 438-7 Part 4.13.3
Thickness increase
%
≤7
Euroclass t ≥ 8mm
Classification
D-s3,d0
–
Euroclass t ≥ 14mm
Classification
–
B-s2,d0
E1
5
3
No damage
≤ 2,5
(A) Maple; Bryna; Ayous Natural; Cherry; Natural Beech; Reconstituted Oak
5. CE Safety requirements - Reaction to fire
Reaction to fire
EN 13.501-1
Panel dimensions
Length (grain direction) x width
* Other thicknesses may be available upon request.
2440 x 1220 mm
Thickness*
8, 11, 14, 17, 20 & 26 mm
2000
Natural timber floor for extreme wear
environments.
Parklex 2000 is a natural timber floating floor made from the
highest quality veneers, impregnated using our exclusive
Gureprex system. This provides extraordinary qualities of
dimensional stability and resistance to both abrasion and
humidity.
Finish range
(1) Panels manufactured from joined timber
veneers. There may be as many as 12 veneer
pieces in each full panel (16 in the case of
stained finishes).
Ambar
Antra
Ayous Natural
Bamboo (1)
Black
Cherry (1)
Eucalyptus (1)
Museum Ash (1)
Grey Beech (1)
Natural Beech (1)
Green Beech (1)
Maple (1)
Walnut (1)
Onix
Natural Oak (1)
Reconstituted Oak (1)
Rubi
Sapelli (1)
Wengue (1)
Natural Zebrano (1)
Surface characteristics
Maintenance and cleaning
Matt. A finish that provides a high quality,
comfortable surface appearance that only
authentic natural timber can provide.
Resistance to abrasion
Resistance to abrasion
Maintenance. The non-porous nature of
the surface prevents the penetration of
dirt. Parklex 2000 requires no specific
stripping or re-finishing.
Cleaning. Mop with water and (neutral)
gel soap.
Assembly systems *
AC4
Floating parquet. Floating installation of
boards glued tongue-in-groove over a
layer of insulation.
Glued. Installation of tongue-in-groove
boards that are adhered to waterproof
DM, using lines of adhesive.
Parquet over underfloor heating. Installation as floating parquet over underfloor
heating.
Panel construction
Gureprex wear resistant overlay
Natural timber veneer
* For more information on installation, consult the Internal Parklex Assembly Catalogue
or our web page (www.parklex.com).
Resin bonded WBP plywood core
HPL balancer
Wood
Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations of
printed media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklex
recommends consulting our sales personnel to request actual samples.
Technical characteristics
Thickness ≥ 11 mm
Tests
Standard
Property or attribute
Measurement unit
Result
Parklex 2000 HDS (Standard)
1. Inspection requirements
Colour, pattern and surface finish
Rev: 04 (09.2009)
EN 438-8 Part 5.2.2.3
Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structure
differences are considered as normal. Singularities such as knots and resin inclusions are not considered as defects,
but as a part of the décor. There are differences in light fastness performances depending on the wood species and
the source of the wood
2. Dimensional tolerances
Gap between pieces
EN 13.329
–
mm
≤ 0,2
Leap between pieces
EN 13.329
–
mm
≤ 0,15
3. Physical properties
≥ AC4
Resistance to surface wear
EN 438-2 Part10
Initial point (PI)
Revolutions
Resistance to inmersion in boiling water
EN 438-2 Part 12
Aspect
Rating
≥4
Impact resistance (small diameter ball)
EN 438-2 Part 20
Force resort
N
≥ 10
Resistance to scratching
EN 438-2 Part 25
Force
Rating
≥3
Resistance to stain
Lightfastness (xenon arc)
EN 438-2 Part26
EN 438-2 Part27
≥ 4.000
Rating (Group 1 & 2)
≥5
Rating (Group 3)
≥4
Aspect
Contrast
≥4
Grey scale rating
< 4 (B)
Resistance to cigarettes burn
EN 438-2 Part 20
Flexural strength
EN 310
Aspect
≥4
Rating
≥ 70
Longrain
Flexural modulus
MPa
Crossgrain
≥ 60
Longrain
≥ 7000
EN 310
MPa
≥ 6000
Crossgrain
Density
-
Density
g/cm3
≥ 0,75
≤5
4. CE Safety requirements
Pentachlorophenol content
EN 438-7 Part 4.10
Content pentachlorophenol
ppm
Release of formaldehyde
EN 717-2
Release of formaldehyde
Rating
E1
Electric resistance
EN 1.081
Vertical resistance
M_
825 (antiestático)
Tendency to accumulation electrostratic charges
EN 1.815
Potential difference
KV
<2
Thermal conductivity
EN 12.524
Conductivity
W/(m*K)
0,17
Water tightness
EN 13.553
Water penetration
Watertight
Slide
EN 13.893
Dynamic coefficient of friction
Classification
_
Slip/skid resistance
UNE-ENV 12.633
Slip resistance value
USRV(Rd)
Clase 1
Euroclass t ≥ 11mm
Classification
Bfl-s1
0,73 (D5)
(A) Maple; Bryna; Ayous Natural; Cherry; Natural Beech; Reconstituted Oak
5. CE Safety requirements - Reaction to fire
Reaction to fire
EN 13.501-1
Package measurements
Contents per package
Minimum no. Panels
m2
Kg
Maximum contents per pallet
No. panels
No. packages
m2
Kg
2440 x 188 x 14 mm*
8
3,68
40
2440 x 290 x 14 mm*
1
0,71
9,5
2440 x 590 x 14 mm*
1
1,44
17
192
24
88,3
960
84
–
59,7
800
42
–
60,7
800
* Standard thickness 14mm. Other thicknesses may be available upon request.
3000
Natural timber finish for full access raised
floors.
Parklex 3000 is a high-density stratified timber panel, impregnated using our exclusive Gureprex system. It may be adhered
to any type of support material (fibreboard, MDF, fibre cement,
galvanised steel etc.) normally used to construct full access
floors.
Finish range
(1) Panels manufactured from joined timber
veneers. There may be as many as 12 veneer
pieces in each full panel (16 in the case of
stained finishes).
Ambar
Antra
Ayous Natural
Bamboo (1)
Black
Cherry (1)
Eucalyptus (1)
Museum Ash (1)
Grey Beech (1)
Natural Beech (1)
Green Beech (1)
Maple (1)
Walnut (1)
Onix
Natural Oak (1)
Reconstituted Oak (1)
Rubi
Sapelli (1)
Wengue (1)
Natural Zebrano (1)
Surface characteristics
Assembly systems *
Matt. A finish that provides a high quality,
comfortable surface appearance that only
authentic natural timber can provide.
Hidden fastening, using adhesive. The
Parklex panels are attached to different
types of supports, using adhesive.
* For more information on installation, consult the Internal Parklex Assembly Catalogue
or our web page (www.parklex.com).
Panel construction
Gureprex wear resistant overlay
Natural timber veneer
HPL balancer
Wood
Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations of
printed media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklex
recommends consulting our sales personnel to request actual samples.
Technical characteristics
Thickness 1 mm
Tests
Standard
Property or attribute
Measurement unit
Result
Parklex 3000 HGS
1. Inspection requirements
Colour, pattern and surface finish
Rev: 03 (09.2009)
EN 438-8 Part 5.2.2.3
Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structure
differences are considered as normal. Singularities such as knots and resin inclusions are not considered as
defects, but as a part of the décor. There are differences in light fastness performances depending on the
wood species and the source of the wood
2. Dimensional tolerances
Thickness (t)
EN 438-2 Part 5
t = 1 mm
mm
± 0,15
Length and width
EN 438-2 Part 6
–
mm
+10 / - 0
Edge straightness
EN 438-2 Part 7
–
mm/m
1,5
Edge squareness
EN 438-2 Part 8
–
mm/m
1,5
Planimetry
EN 438-2 Part 9
–
mm/m
120
Revolutions
0
EN 438-2 Part 10
Resistance to surface wear
Abrasion class
AC4
Initial point
≥ 4.000
Delamination
Pass/ No pass
Pass
Longitudinal
% max
0,75
Transversal
% max
1,25
N
≥ 10
3. Physical properties
Resistance to surface wear
Resistance to inmersion in boiling water
EN 438-2 Part 12
Dimensional stability at high temperatures
EN 438-2 Part17
Impact resistance (small diameter ball)
EN 438-2 Part 20
Force ressort
Resistance to scratching
EN 438-2 Part 25
Force
Resistance to stain
Lightfastness (xenon arc)
EN 438-2 Part26
Rating
≥3
Grupos 1 & 2
≥5
Grupo 3
≥4
Aspect
EN 438-2 Part27
Contrast
Grey scale rating
≥4
< 4 (A)
Resistance to cigarette burns
EN 438-2 Part 30
Aspect
Rating
≥2
Density
EN ISO 1.183
Density
Classification
≥ 1,1
Euroclass
Classification
D-s2,d0 (B)
(A) Maple; Bryna; Ayous Natural; Cherry; Natural Beech; Reconstituted Oak
4. Reaction to fire
Reaction to fire
EN 13.501-1
(B) Composite panels made by a non FIRE RETARDANT HPL adhered to a non fireproof wood substrate.
Panel dimensions *
Standard - Length (grain direction) x width
610 x 610 mm
Maximum - Length (grain direction) x width
2440 x 1220 mm
* Special dimensions available for other applications, upon request.
Thickness
1 mm
Other Parklex products
Facade
External
High-density stratified timber panels for
external use.
Parklex Facade is a high-density stratified timber panel
manufactured from kraft paper treated with resins thermoset
under high pressure and temperature, finished with natural
timber veneers highly resistant to UV radiation and atmospheric
agents.
Parklex Facade includes Everlook®, a special overlay that
dramatically increases the normal life of the panel, improving
UV resistance and colour stability. It also allows for the development of new panels with an extensive range of finishes.
Finish range
Ambar
Antra
Copper
Gold
Surface characteristics
Onix
Quartz
Rubi
Silver
Panel construction
PVDF Antigraffiti overlay
Smooth. Traditional Parklex finish.
Reveals the simple, natural beauty of the
wood it is manufactured with.
Everlook
Natural timber veneer
HPL core
Natural timber veneer
Balancing film
HPL core
NOTE. For more information about this product, consult the
External Parklex Catalogue, the External Parklex Assembly
Catalogue or our web page (www.parklex.com).
Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations of
printed media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklex
recommends consulting our sales personnel to request actual samples.
Applications
1.
2.
3.
1. Semilcos
head office
Vicenza, Italy.
Architect: Pollini+Smania
2. Hospital
Korea.
Architect: Seo hae-cheon
3. Children
Museum
Ireland.
Architect: Traynor O’Toole
4. Alhambra
4.
Information points
Granada, Spain.
Architect: Francisco Martínez Manso, Rafael
Soler Márquez
Facade
700
500
2000
EN/v04/0912
3000
ER-0370/2003
www.parklex.com
COMPOSITES GUREA, S.A. [t ] +34 948 625 045
[f ] +34 948 625 015
Zalain auzoa, 13
31780 Vera de Bidasoa
Navarra (Spain)
[email protected]