Caratterizzazione di fibre di canapa e lino per compositi Milano, 7

Caratterizzazione di fibre di canapa e lino per compositi
A. Aluigi, A. Patrucco, C. Tonin
Milano, 7 giugno 2011
1
Physically, the flax polymer differs from the cotton polymer, in that it has a degree of
polymerisation of about 18 000.
It is about 18 000 nm long and about 0.8 nm thick.
This makes it the longest known, linear textile polymer.
The polymer system of flax is more crystalline than that of cotton and crystals are
smaller.
Flax fibres therefore tend to be stronger, crisper and stiffer to handle, and textile
materials of linen crease (wrinkle) more readily than those of cotton fibres.
2
! "!#
$%%%
3
&
"#
"
#
. +,
! ')
%"-%
'%%")%%
0
$ %" %
! #"$ (
%
"(%
$%"'!
$/
$-%"'-
/'!"! -
* +,
!
!
! '"! (
(%"-%
/%%"!'%%
#! "
* +,
$
$ ((
$'%%" (%%
!
$
!
"
. +,
#%%"!%%%
! "!#
$%%%
4
FIBRE DI CANAPA
CANAPA TECNICA
(per usi industriali)
Fibra tecnica e
canapulo:
Pannelli isolanti
Geotessile
Pannelli truciolari
Lettiere per
animali
Biomassa, pellets
A seconda della destinazione
finale ci sono diversi gradi di
pulizia e processamento delle fibre
Fibra
corta
con
macerazione, cardatura
e separazione a secco
del
canapulo
per
impieghi tecnici (pannelli
di imbottitura oppure
carrozzeria per auto)
CANAPA TESSILE
Fibra lunga con
stigliatura per
l’impiego di qualità
5
6
After retting, the fibre bundles are separated from
the cortex and woody tissue by scutching, which is
a mechanical process carried out to remove some
of the straw from the fiber.
The scutching unit is a process unit in which the
layer of straw is presented through retaining rolls
to a rotating drum with spring steel blades
mounted on its outline. These steel blades on the
outline of the drum have a speed of about 120
km/hour and are scraping off the broken wooden
parts (shives) from the fibres.
In this process the fibre is kept at full length and is
not damaged. The minimum length of the straw
that can be processed is 5 cm; the maximum
length is about 120 cm.
A certain amount of cortical tissue is left adhering to the fibre bundles and gives the
characteristic colour to the raw flax strands.
7
Differenze morfologiche tra canapa e lino
Canapa 400X
Lino 400X
8
ANALISI MORFOLOGICA AL MICROSCOPIO OTTICO
Canapa TECNICA
25X
400X
200X
Canapulo 400X
9
ANALISI MORFOLOGICA AL MICROSCOPIO OTTICO
Canapa TECNICA MACINATA
25X
100X
200X
10
ANALISI MORFOLOGICA AL MICROSCOPIO
ELETTRONICO A SCANSIONE
Canapa TECNICA
Fibra 200 X
Canapulo 400 X
Fibra 200 X
Canapulo 500 X
11
ANALISI MORFOLOGICA AL MICROSCOPIO
ELETTRONICO A SCANSIONE
Canapa TECNICA MACINATA
Fibra 50x
Canapulo 50x
Fibra 100x
Canapulo 100x
12
ANALISI MORFOLOGICA AL MICROSCOPIO OTTICO
Canapa TESSILE
25X
200X
400X
13
Canapa tessile: distribuzione di finezza
14
Lino tessile: distribuzione di finezza
15
Canapa tessile: distribuzione di lunghezza (fibra cotonizzata)
16
Lino tessile: distribuzione di lunghezza (fibra cotonizzata)
17
Caratterizzazione chimico-fisica delle fibre funzionalizzate
- Grado di sostituzione della cellulosa (Tanghe L,J. et. Al.);
- Analisi FTIR ATR;
- Grado di polimerizzazione della cellulosa e della cellulosa esterificata (AFNOR MF T 12-005);
- Ripresa di Umidità delle fibre;
- Analisi morfologica: SEM, TLM, lunghezza e finezza delle fibre (ALMeter e OFDA);
- Proprietà tensili (Stelometer);
- Proprietà termiche;
- ….
18
Caratterizzazione dei compositi
- Analisi FTIR ATR;
- Ripresa di Umidità;
- Angolo di contatto;
- Analisi morfologica: SEM, SEM frattura, TLM, lunghezza delle fibre;
- Proprietà tensili (Instron);
- ….